The invention discloses a lithium ion battery detection method, step 1: injection plastic film to film aluminum in dilute sulfuric acid solution of dilute sulfuric acid solution into the plastic film for pumping and sealing; step 2: Step 1 in plastic film sealing into the oven heating, heating after the plastic film was opened discrimination; the beneficial effect of the invention: the plastic film into the sulfuric acid solution package after heating, the detection method is simple, low detection cost, flexible way to improve the detection rate, can improve the concentration of the sulfuric acid injection, and can quickly and accurately find the damaged position of aluminum plastic film.
【技术实现步骤摘要】
一种锂离子电池用铝塑膜的检测方法
本专利技术涉及锂电池
,特别是涉及一种锂离子电池用铝塑膜的检测方法。
技术介绍
其中铝塑膜作为软包电池的原材料之一是电池厂的必检项目。铝塑膜通常由外层的尼龙层,中间的铝层和内部的PP层组成。最外层的尼龙具有防磨损的作用,中间的铝层起隔绝空气、水分的作用,内部的PP层起隔绝电解液腐蚀、融合封口的作用。在铝塑膜生产制程、运输过程或者模具冲壳过程中,容易产生铝塑膜的PP层破损,从而电解液与铝层接触腐蚀并导致内阻偏大、电芯鼓气、铝塑膜分层甚至破裂漏液等不良现象。目前对于铝塑膜PP层是否破损的检测,尚无快捷有效的方法,通过扫描电镜对铝塑膜进行观察,但此方法观察检测区域较为局限,同时需要特殊仪器,价格较高;或者通过将冲壳后的铝塑膜对照光线,进行目视观察,但部分PP层破损较为细微,肉眼无法识别。
技术实现思路
针对相关技术中的问题,本专利技术提出一种锂离子电池用铝塑膜的检测方法,能够有效解决上述问题。为实现上述技术目的,本专利技术的技术方案是这样实现的:一种锂离子电池用铝塑膜的检测方法,其特征在于,包括以下步骤:步骤1:向膜铝塑内注入稀硫酸溶液,对注入稀硫酸溶液的铝塑膜进行抽气并封口;步骤2:将步骤1中封口的铝塑膜放入烘箱加热,加热完成后拆开铝塑膜进行判别。进一步的,所述步骤1中稀硫酸的质量分数为50%。进一步的,所述步骤1中膜铝塑不加极耳进行封口。进一步的,所述步骤2中烘箱加热温度为60℃,加热时间为15-30分钟。进一步的,所述步骤2中判别方法包括:检查拆开铝塑膜是否有斑点,如果没斑点,则铝塑膜未破损,如果有斑点,则铝塑膜破损,斑 ...
【技术保护点】
一种锂离子电池用铝塑膜的检测方法,其特征在于,包括以下步骤:步骤1:向膜铝塑内注入稀硫酸溶液,对注入稀硫酸溶液的铝塑膜进行抽气并封口;步骤2:将步骤1中封口的铝塑膜放入烘箱加热,加热完成后拆开铝塑膜进行判别。
【技术特征摘要】
1.一种锂离子电池用铝塑膜的检测方法,其特征在于,包括以下步骤:步骤1:向膜铝塑内注入稀硫酸溶液,对注入稀硫酸溶液的铝塑膜进行抽气并封口;步骤2:将步骤1中封口的铝塑膜放入烘箱加热,加热完成后拆开铝塑膜进行判别。2.根据权利要求1所述的一种锂离子电池用铝塑膜的检测方法,其特征在于,所述步骤1中稀硫酸的质量分数为50%。3.根据权利要求2所述的一种锂离子电池用铝塑膜的检测方法...
【专利技术属性】
技术研发人员:孙磊,安富强,
申请(专利权)人:山西长征动力科技有限公司,
类型:发明
国别省市:山西,14