一种钛合金耐磨耐高温涂层的制备方法技术
Preparation of a high temperature resistant coating for titanium alloy
A method for preparing titanium alloy abrasion resistant coating, titanium alloy work piece does not need spraying the surface protection cover, will need to spray the surface exposed; sandblasting on the workpiece surface exposed; by supersonic plasma spraying system and plasma gun, in the surface after washing by spraying a layer of nickel aluminum coating powder coating, coating powder coating is sprayed on the surface layer of nickel cobalt chromium tungsten in aluminum. The invention adopts the method of preparation technology of abrasion resistant coating by supersonic plasma spraying, the coating is dense and uniform surface coating, coating and workpiece good bonding strength, hardness of the coating can meet the requirements, can be very good to meet the high temperature (500 DEG C) wear resistance of technical conditions.
【技术实现步骤摘要】
一种钛合金耐磨耐高温涂层的制备方法
本专利技术涉及一种耐磨耐高温涂层，特别是涉及一种钛合金耐磨耐高温涂层的制备方法。
技术介绍
由于钛合金具有低密度，高比强度和比模量等优势，在航空、航天、生物医疗、石油化工等领域的应用日益广泛，然而因钛合金导热性差、硬度低、耐磨性差、摩擦时易发热粘着等特性，限制了钛合金的应用。如何有效地提高钛合金耐磨性能以及耐高温性能，已成为诸多学者研究的热点。由钛合金材料本身着手进行的提高，受材料标准以及材料特性的限制，已经不能再大幅度提高其耐高温及耐磨性。所以，研究和发展钛合金材料的表面处理技术就具有重大的技术和经济意义。而表面处理技术也在这种需求的推动下得到了快速的发展和提高。热喷涂技术就是其中之一，所谓热喷涂，就是利用某种热源，如电弧、等离子弧、火焰等将粉末状或丝状的金属或非金属喷涂材料加热到熔融或半熔化状态，然后靠热源自身的动力或外加的高速气流雾化并以一定的速度喷射到经过预处理的工件材料表面，依靠喷涂材料的物理变化和化学变化，与工件材料结合而形成具有各种功能的表面覆盖涂层技术。按热源分，热喷涂又分为火焰喷涂、电弧喷涂、等离子喷涂和激光喷...
【技术保护点】
一种钛合金耐磨耐高温涂层的制备方法，其特征在于，包括以下步骤：1)工件表面保护：将钛合金工件不需要喷涂的表面遮盖保护，将需喷涂的表面暴露出来；2)喷砂粗化：对暴露的工件表面进行喷砂粗化；3)热喷涂：采用超音速等离子喷涂系统和等离子喷枪，在清洗后的表面喷涂一层镍铝包覆粉涂层，在镍铝包覆粉涂层上喷涂钴铬钨面层。
【技术特征摘要】
1.一种钛合金耐磨耐高温涂层的制备方法，其特征在于，包括以下步骤：1)工件表面保护：将钛合金工件不需要喷涂的表面遮盖保护，将需喷涂的表面暴露出来；2)喷砂粗化：对暴露的工件表面进行喷砂粗化；3)热喷涂：采用超音速等离子喷涂系统和等离子喷枪，在清洗后的表面喷涂一层镍铝包覆粉涂层，在镍铝包覆粉涂层上喷涂钴铬钨面层。2.根据权利要求1所述的一种钛合金耐磨耐高温涂层的制备方法，其特征在于，喷砂粗化后的工件表面粗糙度Ra≥12.5um。3.根据权利要求1所述的一种钛合金耐磨耐高温涂层的制备方法，其特征在于，喷涂的工艺参数为：功率为40～60KW...