The invention discloses a resin composite dispersing agent by chelating dispersant and heavy metal chelating agent and dispersing agent according to the mass ratio of 1:1:2 is formulated into a mixed suspension liquid, chelating dispersant for maleic anhydride acrylic copolymer; heavy metal chelating agent is two dithiocarbamate derivatives; dispersing agent for the ethoxy modified silicone in three, when the production of anchoring agent of clay composite dispersant resin according to the amount of 2 and 6% resin into the cabin cement premix mixing. The metal chelated metal ion chelating agent can effectively fill in powder such as iron and aluminum ions to prevent the reaction in Anchorage, wetting dispersant filler particles can quickly fully, reduce the interfacial tension, prevent the settlement of solid particles and condensation; using the composite dispersant curing parameters were not obvious drift resin anchoring agent, which greatly reduces the probability of false coagulation phenomenon, to ensure the quality of resin, and filler in the same quality of content on the basis of the original increase by more than 10%, effectively reducing the cost.
【技术实现步骤摘要】
一种树脂锚固剂用复合分散剂
本专利技术涉及一种树脂锚固剂用复合分散剂，具体涉及不饱和聚酯树脂锚固剂领域。
技术介绍
不饱和聚酯树脂锚固剂广泛用于煤矿的煤壁、顶板支护，隧道的顶板支护，井筒安装和建筑物的抗震加固等方面，是支护行业的一个重要组成部分。树脂锚固剂的有效期是三个月，但出厂后并一定被使用方立马使用，往往要存放相当长的时间。在此过程中，锚固剂树脂组份中的阻聚剂的慢慢消耗和采用的促进固化体系的局限性以及填料中含有的金属杂质导致锚固剂的凝胶时间、固化时间、放热峰值等的固化工艺参数发生变化，我们称为固化工艺参数的“漂移”，随储存条件的不同和时间的长短，漂移的程度有所不同。特别严重的在夏季时因石粉填料中含有的高比例金属杂质，导致在锚固剂生产过程中可能还会出现假凝现象，使锚固剂的实际凝胶时间比设计的快很多，并且没有放热量，抗压强度很低，严重的影响了树脂锚固剂的质量，另外，随着树脂锚固剂大幅度的推广使用，需求量日益增加，加上生产厂家的有益竞争，市场对生产成本的要求也日渐苛刻。无疑，增加填料的添加量是最有效而直接的降成本方法，但在保证产品质量的各项技术指标均要符合行业标准要...
【技术保护点】
一种树脂锚固剂用复合分散剂，其特征在于：由螯合分散剂和重金属螯合剂以及超分散剂按质量比1:1:1.8‑2.2的比例配制成混合悬浮液体得到。
【技术特征摘要】
1.一种树脂锚固剂用复合分散剂，其特征在于：由螯合分散剂和重金属螯合剂以及超分散剂按质量比1:1:1.8-2.2的比例配制成混合悬浮液体得到。2.根据权利要求1所述的树脂锚固剂用复合分散剂，其特征在于：由螯合分散剂和重金属螯合剂以及超分散剂按质量比1:1:2的比例配制成混合悬浮液体得到。3.根据权利要求1所述的树脂锚固剂用复合分散剂，其特征在于：所述的螯合分散剂为马来酸...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。