The invention discloses a melamine resin foam and preparation method of hot press molding, which comprises the following raw materials in parts by weight: melamine formaldehyde resin 150~200; foaming agent 5~15; surfactant 5~10; flame retardant 3~10; hole agent 5~12; curing agent 3~6; through the following steps: Taking melamine formaldehyde resin, sequentially adding foaming agent, surface active agent, flame retardant, opening agent and curing agent, mixing evenly, into the microwave foaming furnace for the foam, and then foam cutting, and hot compressed and dried; melamine resin foam tensile strength of the prepared flame retardant, high resistance and not easy off powder, high hole rate, effectively solve the problems existing in the prior art, and the melamine resin foam has good mechanical properties and sound insulation.
【技术实现步骤摘要】
一种热压成型的密胺树脂泡沫及其制备方法
本专利技术属于密胺树脂材料
，具体涉及一种热压成型的密胺树脂泡沫及其制备方法。
技术介绍
三聚氰胺甲醛树脂,又称密胺树脂,是三聚氰胺与甲醛反应得到的聚合物。密胺树脂是一种新型热固性塑料，具有无毒无味、耐腐蚀、耐高温等诸多优点。其分子结构紧密，加工性能好，尺寸稳定，制品外观光滑，有较强的硬度，被广泛应用于日常生活用品、机械、电子等行业。密胺树脂泡沫是以三聚氰胺甲醛树脂为基体，经过特殊的发泡工艺制得的泡沫塑料，具有质轻、无毒、耐高温等面胺树脂的优异性能，虽然有着优异的性能，在生产中占有稳定的地位，但是易于着火燃烧，且防火性较差，不能满足社会发展的要求。密胺树脂虽然自身具有耐热性和阻燃性，但密胺树脂应用场所多为人员密集场所，要求较高，另外还具有脆性较大、易掉粉、强度低等诸多问题，制约了密胺树脂泡沫产品的推广应用。
技术实现思路
本专利技术要解决的技术问题在于提供一种热压成型的密胺树脂泡沫及其制备方法，具有良好的防火阻燃性性，还具有良好的拉伸强度和隔音性。为实现上述目的，本专利技术提供如下技术方案：一种热压成型的密胺树脂泡沫，包括...
【技术保护点】
一种热压成型的密胺树脂泡沫，其特征在于，包括以下重量份数的原料：三聚氰胺甲醛树脂150～200份；发泡剂5～15份；表面活性剂5～10份；阻燃剂3～10份；开孔剂5～12份；固化剂3～6份。
【技术特征摘要】
1.一种热压成型的密胺树脂泡沫，其特征在于，包括以下重量份数的原料：三聚氰胺甲醛树脂150～200份；发泡剂5～15份；表面活性剂5～10份；阻燃剂3～10份；开孔剂5～12份；固化剂3～6份。2.如权利要求1所述的一种热压成型的密胺树脂泡沫，其特征在于，所述发泡剂为正丁烷、正戊烷、正己烷或二氯四氟乙烷的任意一种或几种。3.如权利要求1所述的一种热压成型的密胺树脂泡沫，其特征在于，所述表面活性剂为十二烷基苯磺酸钠、十二烷基硫酸钠或苯磺酸钠。4.如权利要求1所述的一种热压成型的密胺树脂泡沫，其特征在于，所述阻燃剂为磷酸三丁酯、磷酸三(2-乙基己基)酯、磷酸三(2-氯乙基)酯、磷酸三(2，3-二氯丙基)酯、磷酸三(2，3-二溴丙基)酯、磷酸甲苯-二苯酯、磷酸...
【专利技术属性】
技术研发人员：李洋洋，樊雪子，王永飞，李磊磊，刘军飞，刘振涛，左耀卫，付超峰，
申请(专利权)人：郑州峰泰纳米材料有限公司，
类型：发明
国别省市：河南,41