The present invention provides a modified polytetrafluoroethylene composite filled with barium sulfate. It belongs to the technical field of plastic products. The invention comprises the following steps: preparation of A, the activation of barium sulfate and coupling agent mixing, prepared surface containing barium sulfate instead of lipophilic groups, B, mixing the modified barium sulfate and PTFE mixed evenly, high temperature drying, mixed materials reserve, C, billet, will the mixture into a mould, pressed into green, green sintered at high temperature. The invention has no black core inside, and is a kind of gasket material and sealing material with excellent compression and rebound properties.
【技术实现步骤摘要】
硫酸钡填充改性的聚四氟乙烯复合材料
本专利技术属于塑料制品
，涉及一种硫酸钡填充改性的聚四氟乙烯复合材料。
技术介绍
聚四氟乙烯高度的化学稳定性赋予了其制品具有耐强碱强酸、耐高温等特性，是现代科学技术中解决许多关键密封问题不可或缺的材料，但其线膨胀系数大，抗蠕变性能差，使其应用范围受到限制。硫酸钡具有密度大，化学性质稳定，可吸收X射线和γ射线，在自然界中以重晶石存在，具有管状结构。中国专利公开了一种聚四氟乙烯/硫酸钡复合材料及其制备方法[申请号：201610452784.0]，不仅使用钢纤维、碳纤维来提高聚四氟乙烯的抗拉伸强度、摩擦性能，同时利用改进过的熔融法将细的填料如SiO2、Al粉等在高温下烧结到聚四氟乙烯表面，改善了聚四氟乙烯的表面烧结状态，使胶接强度得到明显提高。此外，还应用芥酸酰胺、硫酸钡改善了材料的光泽和生物相容性。但是，申请人用该方案进行制备时，发现在复合材料内部会出现黑芯，导致整体结构强度受到影响。
技术实现思路
本专利技术的目的是针对上述问题和缺陷，提供一种硫酸钡填充改性的聚四氟乙烯复合材料。一种硫酸钡填充改性的聚四氟乙烯复合材料，包括以下制...
【技术保护点】
一种硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于,包括以下制备步骤：A、活化，将硫酸钡与偶联剂搅拌均匀，制得表面含有亲油基团的改性硫酸钡，B、混料，将改性硫酸钡与PTFE混合均匀，高温下烘干，得混合料备用，C、制坯，将混合料放入模具中压制成生坯，生坯在高温下烧结。
【技术特征摘要】
1.一种硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于,包括以下制备步骤：A、活化，将硫酸钡与偶联剂搅拌均匀，制得表面含有亲油基团的改性硫酸钡，B、混料，将改性硫酸钡与PTFE混合均匀，高温下烘干，得混合料备用，C、制坯，将混合料放入模具中压制成生坯，生坯在高温下烧结。2.根据权利要求1所述的硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于，在步骤A中，所述的偶联剂为钛酸酯偶联剂NDZ-401，并加无水乙醇稀释成5-50wt％的偶联剂溶液。3.根据权利要求2所述的硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于，所述的偶联剂溶液中含有钛酸酯偶联剂NDZ-401为10-20wt％。4.根据权利要求3所述的硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于，所述的偶联剂溶液中含有钛酸酯偶联剂NDZ-401为13wt％。5.根据权利要求2所述的硫酸钡填充改性的聚四氟乙烯复合材料，其特征在于，硫酸钡加热至90℃，所述的偶联剂...