The invention discloses a photocatalytic medical packaging film for outdoor, it is composed of the following raw materials: two formic acid butyl ester two 4 6, 40 50, four butyl titanate calcium silicate three 2 3, 5, 3 rosin maleic acid butyl ester two 4, 2 2 mercaptobenzene 0.7 and 1, imidazole castor oil acid 1 calcium 2, UV resistant polymer solution 10 14, 10 15% 5 6 ammonia, PTFE 110 120, the invention of the UV resistant polymer solution and rosin sol blending, to enhance the effect of effective viscosity. Improve the overall stability of the packaging film, UV resistant polymer of the present invention to effectively improve the effect of resistance to UV, prevent packaging film rapid aging.
【技术实现步骤摘要】
一种户外用光催化医用包装膜及其制备方法
本专利技术属于包装膜领域，具体涉及一种户外用光催化医用包装膜及其制备方法。
技术介绍
塑料薄膜是现在人们常见的生活用品，塑料薄膜具有透明性好、阻湿性好、耐热性优良、使用方便、价格便宜等优点被广泛应用于各行各业，目前市场上的塑料薄膜主要以聚乙烯、聚四氟乙烯、聚碳酸酯等塑料薄膜为主，但是有的产品的会出现褶皱、透明度差、厚度不均匀、膜泡鱼眼多等问题，同时，随着人们环保意识的逐渐增强，塑料膜的重复利用率也就越来越高，因此，对于其抗撕裂强度的要求也就更高。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种户外用光催化医用包装膜及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种户外用光催化医用包装膜，它是由下述重量份的原料组成的：苯二甲酸二丁酯4-6、钛酸四丁酯40-50、硅酸三钙2-3、松香3-5、马来酸二丁酯2-4、2-巯基苯并咪唑0.7-1、蓖麻油酸钙1-2、抗紫外聚合物溶液10-14、10-15％的氨水5-6、聚四氟乙烯110-120。所述的抗紫外聚合物溶液是由下述重量份的原料组成的：丙烯酸甲酯17-...
【技术保护点】
一种户外用光催化医用包装膜，其特征在于，它是由下述重量份的原料组成的：苯二甲酸二丁酯4‑6、钛酸四丁酯40‑50、硅酸三钙2‑3、松香3‑5、马来酸二丁酯2‑4、2‑巯基苯并咪唑0.7‑1、蓖麻油酸钙1‑2、抗紫外聚合物溶液10‑14、10‑15％的氨水5‑6、聚四氟乙烯110‑120。
【技术特征摘要】
1.一种户外用光催化医用包装膜，其特征在于，它是由下述重量份的原料组成的：苯二甲酸二丁酯4-6、钛酸四丁酯40-50、硅酸三钙2-3、松香3-5、马来酸二丁酯2-4、2-巯基苯并咪唑0.7-1、蓖麻油酸钙1-2、抗紫外聚合物溶液10-14、10-15％的氨水5-6、聚四氟乙烯110-120。2.根据权利要求1所述的一种户外用光催化医用包装膜，其特征在于，所述的抗紫外聚合物溶液是由下述重量份的原料组成的：丙烯酸甲酯17-20、甲基丙烯酸乙酯20-30、苯并三氮唑1-2、二乙烯基苯0.1-0.2、聚丙烯酰胺3-4、引发剂0.7-1。3.根据权利要求2所述的一种户外用光催化医用包装膜，其特征在于，所述的抗紫外聚合物溶液的制备方法，包括以下步骤：(1)取引发剂，加入到其重量20-30倍的去离子水中，搅拌均匀；(2)取苯并三氮唑，加入到其重量4-6倍的无水乙醇中，搅拌均匀，加入二乙烯基苯，搅拌均匀，得交联溶液；(3)取聚丙烯酰胺，加入到其重量20-30倍的去离子水中，搅拌均匀；(4)取丙烯酸甲酯、甲基丙烯酸乙酯混合，加入到混合料重量10-13倍的去离子水中，搅拌均匀，送入到反应釜中，...