一种电池箱及该电池箱、电池箱体的成型方法技术
A molding method for a battery box and the battery box and battery box
The invention relates to a method for forming a battery box and the battery box, a battery box, a battery box forming method comprises the following steps: 1) at set position will support and the glass fiber cloth into the battery box mold; 2) through hot pressing processing into the battery box. Compared with the prior art, the method of hot press molding glass fiber cloth and support integrated, simple process, high structural strength, heat resistance and corrosion resistance, air tightness performance can be improved, and implementation of the lightweight battery box, low cost, and is beneficial to mass production and widespread use.
【技术实现步骤摘要】
一种电池箱及该电池箱、电池箱体的成型方法
本专利技术涉及一种电池箱及该电池箱、电池箱体的成型方法。
技术介绍
随着国家对新能源行业扶持政策的调整，动力电池企业对电池箱的结构、拉伸强度、重量、气密性、耐腐蚀性等方面提出了更多的要求。电池箱包括电池箱体和箱盖，目前行业多采用铸铝电池箱体或钢板焊接电池箱体，铸铝电池箱体由于铸造工艺复杂，易产生电池箱缺陷，影响电池箱的气密性，同时废品率及生产成本较高；钢板焊接电池箱的加工工艺复杂，重量较大，密封性能不佳，且耐腐蚀性差，无法满足行业轻量化要求。
技术实现思路
本专利技术的目的在于提供一种电池箱，以解决现有技术中的电池箱铸造工艺复杂、密封性能不佳以及耐腐蚀性差的问题；本专利技术的目的还在于提供一种该电池箱、电池箱体的成型方法。为实现上述目的，本专利技术电池箱体的成型方法的第一种技术方案是：电池箱体的成型方法，包括以下步骤，1）将支撑件和玻璃纤维布放入电池箱体成型模具的设定位置处；2）通过热压成型工艺加工成电池箱体。本专利技术电池箱体的成型方法的第二种技术方案是：在本专利技术电池箱体的成型方法的第一种技术方案的基础上，在步骤1）中，...
【技术保护点】
电池箱体的成型方法，其特征在于：包括以下步骤，1）将支撑件和玻璃纤维布放入电池箱体成型模具的设定位置处；2）通过热压成型工艺加工成电池箱体。
【技术特征摘要】
1.电池箱体的成型方法，其特征在于：包括以下步骤，1）将支撑件和玻璃纤维布放入电池箱体成型模具的设定位置处；2）通过热压成型工艺加工成电池箱体。2.根据权利要求1所述的电池箱体的成型方法，其特征在于：在步骤1）中，把第一层玻璃纤维布和支撑件放入电池箱体成型模具的设定位置处，然后再在第一层玻璃纤维布上叠加多层玻璃纤维布；或者将叠加好的多层玻璃纤维布直接和支撑件放入电池箱体成型模具的设定位置处。3.根据权利要求2所述的电池箱体的成型方法，其特征在于：在步骤1）中，先将支撑件放入电池箱体成型模具的设定位置处，再将第一层玻璃纤维布的表面涂覆粘接剂，把玻璃纤维布放入电池箱体成型模具，通过粘接剂的渗透使支撑件与玻璃纤维布粘接预固定。4.电池箱的成型方法，其特征在于：包括以下步骤，1）将支撑件和玻璃纤维布放入电池箱体成型模具的设定位置处；2）通过热压成型工艺加工成电池箱体；3）将电池箱体和箱盖密封连接。5.根据权利要求4所述的电池箱的成型方法，其特征在于：在步骤1）中，把第一层玻璃纤维布和支撑件放入电池箱体成型...
【专利技术属性】
技术研发人员：李炜，王鑫淼，谢秋，曹勇，杨大鹏，庄文波，尹玉鑫，
申请(专利权)人：中航锂电洛阳有限公司，中航锂电技术研究院有限公司，
类型：发明
国别省市：河南,41