复合焊丝，属于焊接材料技术领域。本发明专利技术是为了解决现有单丝焊丝焊接由于焊缝两边受热较低，形成焊缝向上凸起，焊接质量低的问题。它包括：内层的焊材；包裹焊材的外层的钢皮；还可以包括填充在焊材与钢皮之间的焊剂。本发明专利技术作为一种复合焊丝，外层的钢皮直接参与焊接过程中的填充，能增加金属填充量，具有高溶覆率，从而提高焊接效率。

Composite wire

The composite welding wire belongs to the technical field of welding material. The present invention is to solve the problem that the welding quality of the existing monofilament welding wire is low due to low heat of the weld on both sides of the weld, and the welding seam is raised upward and the welding quality is low. It includes: the inner skin coated steel welding consumables; welding; can also include filling between the welding materials and steel flux. As a composite welding wire, the outer layer of steel skin directly participates in the filling process during welding. It can increase the amount of metal filling, and has high dissolving rate, so as to improve the welding efficiency.

【技术实现步骤摘要】
复合焊丝
本专利技术涉及复合焊丝，属于焊接材料

技术介绍
采用传统的单丝焊丝进行焊接时，电弧对工件的加热一般都是由中间开始，熔池从中心向外扩散，这种方式造成焊缝的中间温度高，周边温度低。由于表面张力的作用，焊缝会向上凸起。对于多层多道焊接，由于电弧对焊缝的中心位置加热多，而两边加热少，很容易造成焊缝两边夹渣或熔合不良的情况。
技术实现思路
本专利技术是为了解决现有单丝焊丝焊接由于焊缝两边受热较低，形成焊缝向上凸起，焊接质量低的问题，提供了一种复合焊丝。本专利技术所述复合焊丝，它包括：内层的焊材；包裹焊材的外层的钢皮。还包括填充在焊材与钢皮之间的焊剂。所述焊材为单股实芯丝，单股实芯丝与钢皮同轴设置。或者所述焊材为多股实芯丝。所述多股实芯丝其中的一股作为中心股与钢皮同轴设置，其余股沿圆周方向均匀的环绕在中心股周围。或者所述多股实芯丝沿焊材的宽度方向等距离的排布成一条直线。本专利技术的优点：本专利技术所述复合焊丝，其外层的钢皮也直接参与焊接过程中的填充，能增加金属填充量，具有高溶覆率，从而提高焊接效率。附图说明图1是本专利技术所述包括单股实芯丝的复合焊丝的结构示意图；图2是本专利技术本文档来自技高网...

【技术保护点】
一种复合焊丝，其特征在于，它包括：内层的焊材；包裹焊材的外层的钢皮。

【技术特征摘要】
1.一种复合焊丝，其特征在于，它包括：内层的焊材；包裹焊材的外层的钢皮。2.根据权利要求1所述的复合焊丝，其特征在于，还包括：填充在焊材与钢皮之间的焊剂。3.根据权利要求1或2所述的复合焊丝，其特征在于，所述焊材为单股实芯丝，单股实芯丝与钢皮同轴设置。4.根据权利要求1或2所述的复合焊丝，其特征在于，所述焊材为多股实...

【专利技术属性】
技术研发人员：邓惠芬，
申请(专利权)人：邓惠芬，
类型：发明
国别省市：广东,44