The invention relates to a neodymium iron boron magnet coated with interpenetrating polymer network coating and a preparation method thereof, including sintered Nd-Fe-B magnet, and the surface of sintered NdFeB magnet is coated with an interpenetrating polymer network coating with a thickness of 11 mu m~19 m. It is made by coarsening and preparing the interpenetrating polymer coating size, coating treatment and curing process. Sintered Nd-Fe-B magnets coated with interpenetrating polymer network coatings have excellent properties of high temperature resistance, high pressure resistance, anti-aging, corrosion resistance and strong adhesion.
【技术实现步骤摘要】
一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体及制备方法
本专利技术涉及磁性材料表面防护领域，具体涉及一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体及制备方法。
技术介绍
烧结钕铁硼磁体具有优异的剩磁、矫顽力和磁能积，被称为当代“磁王”，因此被广泛应用于五金电器、医疗器械、风力发电、汽车、航空航天、尖端科技等诸多领域。烧结钕铁硼磁体是稀土永磁材料的支柱，但烧结钕铁硼磁体由主相Nd2Fe14B、富Nd相和富B相组成，其中金属Nd元素的化学活性最强，在潮湿、高温以及电化学环境中极易被腐蚀，严重限制了烧结钕铁硼磁体应用领域的进一步拓展。工业上一般采用有机聚合物进行表面防护，当前行业普遍采用的阴极电泳环氧树脂涂层具有厚度一致性高，涂层与基体结合力强、耐酸、碱性能优异等优点，但该涂层硬度较小，耐磨性能极差，在包装及运输过程中易发生破损。由于环氧树脂涂层为阴极防护涂层，一旦涂层发生破损，磁体将遭受严重的腐蚀，造成磁体表面防护涂层的失效防护。互穿网络聚合物涂层是由两种或两种以上的聚合物通过网络互穿缠结而形成的一种新型共混合或聚合物涂层，由于各聚合物网络之间的相互交叉渗透、机械缠结有效改...
【技术保护点】
一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体，其特征在于：包括烧结钕铁硼磁体,所述烧结钕铁硼磁体的表面涂覆有一层厚度为11μm~19μm的互穿网络聚合物涂层。
【技术特征摘要】
1.一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体，其特征在于：包括烧结钕铁硼磁体,所述烧结钕铁硼磁体的表面涂覆有一层厚度为11μm~19μm的互穿网络聚合物涂层。2.根据权利要求1所述的一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体，其特征在于：所述互穿网络聚合物涂层是由以下材料按质量百分比组成：环氧树脂40%~50%、聚氨酯30%~40%、聚硅氧烷10%~20%、添加剂2%~5%、溶剂补充至100%。3.根据权利要求2所述的一种涂覆互穿网络聚合物涂层的烧结钕铁硼磁体，其特征在于：所述添加剂是甲苯二异氰酸酯、炭黑和过氧化二苯甲酰中的一种，所述溶剂为二甲苯-丁醇。4.一种如权利要求1-3任意一项所述的涂覆互穿网络聚合物涂层的烧结钕铁硼磁体的制备方法，其特征在于：包括以下步骤：a.粗化处理：对烧结钕铁硼磁体表面粗化处理；b.将环氧树脂40%~50%、聚氨酯30%~40%、聚硅氧烷10%~20%、添加剂2%~5%、溶剂补充至100%，于80℃~100℃温度下进行搅拌混合，得互穿网络聚合物涂层浆料；c.涂覆处理：采用喷涂方式在烧结钕铁硼磁体表面涂覆一层互穿网络聚合物涂层浆料，其涂覆厚度为11μm~19μm；d.固化处理：对涂覆后的烧结钕铁硼磁体进行固化处理。5...
【专利技术属性】
技术研发人员：张鹏杰，曹玉杰，吴玉程，黄秀莲，陈静武，衣晓飞，
申请(专利权)人：安徽大地熊新材料股份有限公司，
类型：发明
国别省市：安徽,34