The present invention discloses antibacterial pollution resistant PVDF ultrafiltration membrane for water filtration, calculated in accordance with the quality mainly comprises the following components: PVDF: 100; 15: polyethylene glycol 35; silver loaded chitosan: 3 15. The present invention by solution blending polyvinylidene fluoride and polyethylene glycol mixed in the N methylpyrrolidone dissolved; chitosan was prepared by silver loaded chitosan solution, the PVDF membrane was immersed in silver loaded chitosan solution, after drying can be prepared by hydrophilic antimicrobial resistance the pollution of PVDF microporous membrane. The polyvinylidene fluoride microporous membrane prepared by the invention not only has better hydrophilicity, but also destroys surface microbes, reduces the amount of protein attachment in the sewage, and can deactivate the protein and prolong the service life of the polyvinylidene fluoride membrane effectively.
【技术实现步骤摘要】
一种水过滤用抗菌耐污染的PVDF超滤膜
本专利技术属于水过滤用的聚偏氟乙烯过滤膜的
，具体涉及一种水过滤用抗菌耐污染的PVDF超滤膜。
技术介绍
聚偏氟乙烯具有优良的化学稳定性、耐辐射性、耐热性和易成膜等特点，然而聚偏氟乙烯的表面自由能较低，聚偏氟乙烯膜的表面亲水性较差，聚偏氟乙烯作为水处理膜时容易被污染，导致PVDF水处理膜的通量下降、分离效果降低，增加了清洗难度、降低了膜的使用寿命。所述PVDF水处理膜的表面为疏水性，污水中含有的胶体、蛋白质和其他有机物质，容易附着在PVDF膜表面形成污染层，使得膜的水通量急剧下降。所述蛋白质附着在PVDF表面后会继续生长附着其他的蛋白质，日积月累，所述PVDF膜的表面会形成一层微生物膜，所述PVDF膜净化水质的同时会对水质进行二次污染。现有技术通过物理或者化学改性PVDF膜的表面亲水性，然而简单的改性PVDF膜的亲水性不能有效的杀灭附着滋生的微生物菌。
技术实现思路
本专利技术的目的在于提供一种水过滤用抗菌耐污染的PVDF超滤膜，按照质量份计算主要包括以下成分：聚偏氟乙烯：100份；聚乙二醇：15-35份；载银壳聚糖：3-...
【技术保护点】
一种水过滤用抗菌耐污染的PVDF超滤膜，其特征在于，按照质量份计算主要包括以下成分：聚偏氟乙烯：100份；聚乙二醇：15‑35份；载银壳聚糖：3‑15份。
【技术特征摘要】
1.一种水过滤用抗菌耐污染的PVDF超滤膜，其特征在于，按照质量份计算主要包括以下成分：聚偏氟乙烯：100份；聚乙二醇：15-35份；载银壳聚糖：3-15份。2.根据权利要求1所述的一种水过滤用抗菌耐污染的PVDF超滤膜，其特征在于，所述载银壳聚糖的载银量为240mg/g-300mg/g。3.根据权利要求2所述的一种水过滤用抗菌耐污染的PVDF超滤膜，其特征在于，所述载银壳聚糖中含有0.8wt%-2wt%的交联剂。4.根据权利要求1所述的一种水过滤用抗菌耐污染的PVDF超滤膜，其特征在于，所述聚乙二醇的型号为PGE-20000。5.根...