Preparation method of TB6 alloy powder, which comprises the following steps: 1, TB6 master alloy rod melting; step 2, the TB6 alloy rods after processing electric rod diameter of 10 90mm, length of 100 1000mm; step 3, the electrode rod set of inert gas reaction chamber and high speed by rotation, plasma gun power is 100 300KW heating electrode rod end, the electrode rod end melt; step 4, after the atomization of molten metal under the action of centrifugal force to fly, the formation of small droplets, droplet in protective gas fast cooling after the formation of spherical particles into the spray chamber at the bottom of the collector. TB6 alloy powder; preparation of TB6 alloy powder, has the characteristics of high roundness, good liquidity.
【技术实现步骤摘要】
一种TB6合金球形粉末的制备方法
本专利技术属于合金球形粉末制备
，具体涉及一种TB6合金球形粉末的制备方法。
技术介绍
钛及钛合金作为结构金属，具有比强度高、抗腐蚀性好、耐高温等一系列突出优点，能够进行多种方式的压力加工成形、焊接和机械加工。随着钛合金研究和生产的发展，被广泛应用于航空航天等领域，如涡轮发动机和飞机构架等关键部位。TB6合金属于高V当量的近β钛合金，具有比强度高、热稳定性好、抗蠕变性能优异和可焊性强等优点，被广泛地应用于航空航天工业中关键零部件的制造。采用传统的锻造和铸造方法生产TB6钛合金成材率低，容易产生废料，从而导致了TB6合金的生产成本较高。此外，传统铸锻工艺很难直接制造出具有复杂形状的零件，经过后续的加工处理后，材料利用率（Buy-to-fly-ratio）进一步降低，同时大幅增加了生产周期。粉末冶金制备方法是一种具有工艺流程短、材料利用率高、组织细小均匀、成分可控等优点的近净成形技术，可以克服传统加工方法的缺陷，但是粉末冶金对粉末的性能要求苛刻，传统的方法制备的粉末品质与批次稳定性普遍较差。粉末的圆形度是影响粉末性能（包括流动性...
【技术保护点】
一种TB6合金球形粉末的制备方法，按质量百分比，其特征在于，包括以下步骤：步骤1，TB6母合金棒的熔炼；合金成分按照GB/T3620‑2016进行配比；步骤2，将步骤1的TB6合金母合金棒坯制成电极棒，电极棒直径为10‑90mm，长度为100‑1000mm，电极棒直线度偏差控制在≤0.1mm/m；步骤3，将电极棒置于惰性气体密闭反应室内并高速旋转，采用等离子枪加热电极棒端部，使其融化；步骤4，步骤3的电极棒端部金属雾化后在离心力作用下飞出，形成细小液滴，液滴在保护气体中快冷后形成球形颗粒，落入雾化室底部收集容器内，得到TB6合金球形粉末。
【技术特征摘要】
1.一种TB6合金球形粉末的制备方法，按质量百分比，其特征在于，包括以下步骤：步骤1，TB6母合金棒的熔炼；合金成分按照GB/T3620-2016进行配比；步骤2，将步骤1的TB6合金母合金棒坯制成电极棒，电极棒直径为10-90mm，长度为100-1000mm，电极棒直线度偏差控制在≤0.1mm/m；步骤3，将电极棒置于惰性气体密闭反应室内并高速旋转，采用等离子枪加热电极棒端部，使其融化；步骤4，步骤3的电极棒端部金属雾化后在离心力作用下飞出，形成细小液滴，液滴在保护气体中快冷后形成球形颗粒，落入雾化室底部...
【专利技术属性】
技术研发人员：闫飞，韩志宇，王庆相，梁书锦，张平祥，
申请(专利权)人：西安欧中材料科技有限公司，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。