The invention discloses an environment-friendly rubber high temperature resistant and corrosion resistant, made from the following raw materials according to the quality plan number 80: natural rubber 100, stabilizer 8 15 25 40, nitrile rubber, chloroprene rubber modified 20 50 carbon black, 15 30, 8 polystyrene 12, curing agent 1 1.5, stearic acid 2 4, 5 Zinc Oxide 10, Magnesium Oxide 12 18, 10 antioxidant 14, flame retardant 15 25, 20 paraffin 30, 4 accelerator 5. Through the simple preparation method of temperature corrosion protection rubber rubber, not only low cost, anti chemical corrosion effect is good, and simple preparation process, easy industrialization, and has excellent stability, heat resistance, and non-toxic, environmental protection, can effectively reduce environmental pollution, long service life.
【技术实现步骤摘要】
一种耐高温耐腐蚀的环保橡胶
本专利技术涉及橡胶领域，具体的说，是一种耐高温耐腐蚀的环保橡胶。
技术介绍
橡胶具有可逆形变的高弹性聚合物材料。在室温下富有弹性，在很小的外力作用下能产生较大形变，除去外力后能恢复原状。橡胶属于完全无定型聚合物，它的玻璃化转变温度（Tg）低，分子量往往很大，大于几十万。橡胶为高弹性聚合物，其分子结构为链状，分子链具有较高的柔性。橡胶的分子链可以交联（硫化），交联后的材料，受外力作用发生形变时，具有迅速复原的能力，并具有良好的物理机械性能及化学稳定性。橡胶只有经过交联才能成为有使用价值的高弹性材料，俗称橡皮。橡胶是橡胶工业的基础原料，广泛用于制造轮胎、胶管、胶带、电缆及其他各种橡胶制品。它与金属、化学纤维、塑料等同为重要的材料。通常橡胶本身不耐火。而目前火灾事故中，发生电线电缆不耐火，遇火易燃烧问题，本领域缺乏一种耐火的橡胶，要求能在大火中起到一定的保护作用，能够减少火灾中电给人们带来的损失，减少电的危害。耐火橡胶是以氯丁二烯为主要原料，通过均聚或少量其它单体共聚而成的。如抗张强度高橡胶制品，耐热、耐光、耐老化性能优良，耐油性能均优于天然...
【技术保护点】
一种耐高温耐腐蚀的环保橡胶，其特征在于：由如下按照质量份数计的原料制成：天然橡胶80‑100，稳定剂8‑15，丁腈橡胶25‑40，改性氯丁橡胶20‑50，炭黑15‑30，聚苯乙烯8‑12，硫化剂1‑1.5，硬脂酸2‑4，氧化锌5‑10，氧化镁12‑18，防老剂10‑14，阻燃剂15‑25，石蜡20‑30，促进剂4‑5。
【技术特征摘要】
1.一种耐高温耐腐蚀的环保橡胶，其特征在于：由如下按照质量份数计的原料制成：天然橡胶80-100，稳定剂8-15，丁腈橡胶25-40，改性氯丁橡胶20-50，炭黑15-30，聚苯乙烯8-12，硫化剂1-1.5，硬脂酸2-4，氧化锌5-10，氧化镁12-18，防老剂10-14，阻燃剂15-25，石蜡20-30，促进剂4-5。2.根据权利要求1所述的一种耐高温耐腐蚀的环保橡胶，其特征在于：所述硫化剂为硫磺、过氧化二异丙苯中的一种或者硫磺和过氧化二异丙苯的组合物。3.根据权利要求1所述的一种耐高温耐腐蚀的环保橡胶，其特征在于：所述的防老剂为N-苯基-α-苯胺、N-苯基-N’-异丙基-对苯二胺、N-N’-二苯基-对苯二胺、防老剂4020中的一种或多种。4.根据权利要求1所述的一种耐高温耐腐蚀的环保橡胶，其特征在于：所述丁腈橡胶按重量份数计，由丁二烯70，丙烯腈34，水150...
【专利技术属性】
技术研发人员：杨素杰，
申请(专利权)人：成都米利得科技有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。