The invention relates to a high strength lightweight partition board and a preparation method thereof, comprising the following raw materials in parts by weight: 8 Portland cement 15, 5 sawdust 10, gypsum powder 6 10 copies, 8 copies, 5 gypsum fiber Magnesium Oxide 2 5 copies, 10 copies of 4 sodium carbonate, 70 80 nano cellulose. The partition board of the invention is plaster fiber, and the advantages of the two components of gypsum fiber are reinforced fiber and superfine inorganic filler. The addition of partition wall can not only play a role of reinforcing and toughening, but also play a role of thermal insulation, flame retardancy, fire and heat insulation. The nano cellulose of the invention contains enzyme powder, and the reaction of nano cellulose and some silicon elements in the cement catalyzes the formation of the composite membrane type super strength and toughness internal structure, so as to greatly improve the bending strength and bending strength of the lightweight cement partition board.
【技术实现步骤摘要】
一种高强度轻质隔墙板及其制备方法
本专利技术涉及建筑材料领域，具体涉及一种高强度轻质隔墙板及其制备方法。
技术介绍
轻质隔墙板是一种新型的节能墙材料，它具有质量轻、强度高、多重环保、保温隔热、呼吸调湿、防火、快速施工、降低墙体成本等优点，故而在建筑室内装修领域备受青睐，然而目前市场上使用的轻质隔墙板存在抗压强度低、抗拉强度弱和抗开裂性能差等缺陷。
技术实现思路
为了解决现有隔墙板抗压强度低、抗拉强度弱和抗开裂性能差等缺陷，本专利技术提供了一种高强度轻质隔墙板及其制备方法。本专利技术是通过以下技术方案实现的：本专利技术一方面提供了一种高强度轻质隔墙板，包括如下重量份数的原料：硅酸盐水泥8-15份、木屑5-10份、石膏粉6-10份、石膏纤维5-8份、氧化镁2-5份、纳米碳酸钠4-10份、纳米纤维素70-80份。进一步的，包括如下重量份数的原料：硅酸盐水泥11份、木屑8份、石膏粉8份、石膏纤维6份、氧化镁3份、纳米碳酸钠7份、纳米纤维素75份。进一步的，所述纳米纤维素的粒径在15000目以上。进一步的，所述纳米纤维素中含有促进纤维素与水泥中的硅反应的酶粉。本专利技术另一方面...
【技术保护点】
一种高强度轻质隔墙板，其特征在于，包括如下重量份数的原料：硅酸盐水泥8‑15份、木屑5‑10份、石膏粉6‑10份、石膏纤维5‑8份、氧化镁2‑5份、纳米碳酸钠4‑10份、纳米纤维素70‑80份。
【技术特征摘要】
1.一种高强度轻质隔墙板，其特征在于，包括如下重量份数的原料：硅酸盐水泥8-15份、木屑5-10份、石膏粉6-10份、石膏纤维5-8份、氧化镁2-5份、纳米碳酸钠4-10份、纳米纤维素70-80份。2.根据权利要求1所述的高强度轻质隔墙板，其特征在于，包括如下重量份数的原料：硅酸盐水泥11份、木屑8份、石膏粉8份、石膏纤维6份、氧化镁3份、纳米碳酸钠7份、纳米纤维素75份。3.根据权利要求1或2所述的高强度轻质隔墙板，其特征在于，所述纳米纤维素的粒径在15000...
【专利技术属性】
技术研发人员：方杰敏，
申请(专利权)人：桂林市漓江机电制造有限公司，
类型：发明
国别省市：广西,45