The invention relates to a glass fiber reinforced material, which comprises the following components by weight: 86~120 parts by weight of silica, strontium carbonate 8~14 weight portions, three to 3~9 parts by weight of two aluminum oxide, polypropylene fiber 12 15 parts by weight of glass fiber, 18 26 weight parts of lignin fiber 3 8 weight portions, oxidation 0.3 to 1.5 parts by weight of samarium neodymium oxide, 0.6 to 3 parts by weight. The fiber reinforced glass material of the invention is reasonable in composition, and has excellent anti shock, explosion protection, mechanical damage and high and low temperature resistance. It plays an explosion-proof effect and improves explosion-proof safety performance.
【技术实现步骤摘要】
一种纤维增强的玻璃材料
本专利技术涉及材料领域，具体的说，涉及一种纤维增强的玻璃材料。
技术介绍
随着科技的发展，需要使用玻璃的场所变得多样化，对玻璃性能指标有了更加严格和多样的要求，不断的提高玻璃的性能，是经济和社会发展的迫切需求。其中，防爆玻璃已经广泛应用在在金融、收费场所、高级会议中心、豪华酒店、博物馆、领事馆以及警用军用安全设施及私家别墅等场合，主要用于防止玻璃破碎四处散开，易对内部人员及家具造成损伤，而防爆玻璃，即使在破碎后，也是整块粘连在一起，不易散开，碎片不会四散。现有的防爆玻璃，一般是由防弹复合夹层玻璃构成，这种结构的防弹玻璃，在受到爆炸的冲击波或是其他外力冲击下，内侧的玻璃碎片容易产生飞溅，这样容易对玻璃后方的人造成伤害。因此，研究一种本身就具有防爆、抗冲击等性能的效果，且综合性能较为优异的纤维增强的玻璃材料，变得十分有必要。
技术实现思路
本专利技术所要解决的技术问题是提供一种纤维增强的玻璃材料。本专利技术解决上述技术问题的技术方案如下：本专利技术提供一种纤维增强的玻璃材料，包括如下重量份的组分：二氧化硅86～120重量份，碳酸锶8～14重量份，三...
【技术保护点】
一种纤维增强的玻璃材料，其特征在于，包括如下重量份的组分：二氧化硅86～120重量份，碳酸锶8～14重量份，三氧化二铝3～9重量份，聚丙烯纤维12‑15重量份，玻璃纤维18‑26重量份，木质素纤维3‑8重量份，氧化钐0.3～1.5重量份，氧化钕0.6～3重量份。
【技术特征摘要】
1.一种纤维增强的玻璃材料，其特征在于，包括如下重量份的组分：二氧化硅86～120重量份，碳酸锶8～14重量份，三氧化二铝3～9重量份，聚丙烯纤维12-15重量份，玻璃纤维18-26重量份，木质素纤维3-8重量份，氧化钐0.3～1.5重量份，氧化钕0.6～3重量份。2.根据权利要求1所述一种纤维增强的玻璃材料，其特征在于，包括如下重量份的组分：二氧化硅86重量份，碳酸锶8重量份，三氧化二铝3重量份，聚丙烯纤维12重量份，玻璃纤维18重量份，木质素纤维3重量份，氧化钐0.3重量份，氧化钕0.6重量份。3.根据权利要求1所述一种纤维增强的玻璃材料，其特征在于，包括如下重量份的组分：二氧化硅120重量份，碳酸锶14重量份，三氧化二铝9重量份，聚丙烯纤维15重量份，玻璃纤维26重量份，木质素纤维8重量份，氧化钐1.5重量份，氧化钕3重量份。4.根据权利要求1所述一种纤维增强的玻璃材料，...
【专利技术属性】
技术研发人员：方杰敏，
申请(专利权)人：桂林市漓江机电制造有限公司，
类型：发明
国别省市：广西,45