The invention discloses a blackening agent for stainless steel. The stainless steel blackening agent is made from deionized water and contains the following components: sodium sulfate 20 ~ 40g/L, sodium nitrate 8 ~ 20g/L, complex complexing agent 17 ~ 26g/L and rare earth salt 1 ~ 5g/L. By adjusting and optimizing the components of the blackening agent, the invention does not contain potassium dichromate, and has no pollution to the environment, and pH is neutral. It has no adverse effects on the workers, and at the same time, it has a short blackening time at room temperature, and the effect of surface scale marking is good. The invention also discloses a method for blackening the stainless steel blackening agent, which has the advantages of environmental protection, room temperature low energy consumption, short work time, the required low working voltage, which is suitable for large-scale industrialized production, and the surface markings effect on 304 stainless steel wire is good.
【技术实现步骤摘要】
一种不锈钢发黑剂、发黑方法
本专利技术涉及表面处理领域，特别涉及一种不锈钢表面处理。
技术介绍
不锈钢导丝是用于介入诊断和治疗用器械的导入的一次性医疗器械。导丝是引导导管置管进入人体的关键部件，采用不锈钢304材料加工制成，需要有表面标记刻度才有利于临床医生手术操作时控制好在血管或其它人体腔道的位置。而不锈钢导丝表面刻度标记目前都是采用不锈钢表面氧化发黑处理技术。现有技术中常用重铬酸钾和硫酸作为不锈钢导丝的发黑剂，这种发黑剂含有重铬酸钾，污染环境，而且发黑处理时需要加热，发黑时间要几分钟到十几分钟，用时较长。且这种发黑剂的腐蚀程度不易控制，在发黑过程中容易造成一些直径在0.43～1mm的不锈钢304导丝发生断裂的风险。
技术实现思路
本专利技术的目的在于针对上述现有技术的不足，提供一种不锈钢发黑剂，其对环境无污染，且常温发黑时间短，表面刻度标记效果良好，同时提供一种使用了该不锈钢发黑剂的发黑方法。本专利技术所采取的技术方案是：一种不锈钢发黑剂，该不锈钢发黑剂以去离子水为溶剂并含有如下组分：硫酸钠20～40g/L、硝酸钠8～20g/L、复合络合剂17～26g/L和稀土盐...
【技术保护点】
一种不锈钢发黑剂，其特征在于，该不锈钢发黑剂以去离子水为溶剂并含有如下组分：硫酸钠20～40g/L、硝酸钠8～20g/L、复合络合剂17～26g/L和稀土盐1～5g/L。
【技术特征摘要】
1.一种不锈钢发黑剂，其特征在于，该不锈钢发黑剂以去离子水为溶剂并含有如下组分：硫酸钠20～40g/L、硝酸钠8～20g/L、复合络合剂17～26g/L和稀土盐1～5g/L。2.根据权利要求1所述的一种不锈钢发黑剂，其特征在于：所述稀土盐为硫酸镧或硫酸铈。3.根据权利要求1所述的一种不锈钢发黑剂，其特征在于：所述复合络合剂由3～8g/L的草酸钠和14～18g/L的柠檬酸钠组成。4.根据权利要求1...
【专利技术属性】
技术研发人员：郑崇，周伟，陈巧霞，
申请(专利权)人：广东百合医疗科技股份有限公司，
类型：发明
国别省市：广东,44