The invention discloses a copper alloy casting process of a burner, the technical scheme of the utility model is implemented as follows: Step 1: use the copper melting induction furnace to molten state; step 2: adding solid magnesium in the liquid copper; step 3: the complete fusion of copper magnesium alloy liquid pouring into alloy rod step 4: alloy casting; rod quick cooling; step 5: prepare the copper alloy casting rod. The invention has the following beneficial effects: the copper and magnesium alloy makes the production cost relatively low, and the melting point of the alloy is lower than that of the pure metal; the conductivity of copper is good; the hardness of the alloy is increased by the metal magnesium, so that the copper alloy casting rod has high tensile strength and wear resistance.
【技术实现步骤摘要】
一种燃烧器用铜合金铸造工艺
本专利技术属于铸造
，具体涉及一种燃烧器用铜合金铸造工艺。
技术介绍
铜既是一个古老的金属，又是一个充满生机和活力的现代工程材料。当前人类步入了丰富多彩的，以电气化和电子信息为特征的，高度文明的社会，为铜的应，用开辟了更为广阔的大地。铜以品种繁多的金属、合金和化合物的形式被人们利用，业已深深地渗入了生产和生活的各个方面，铜合金具有良好的导热性能，尤其被用于燃烧器的制造和使用方面，因而成为人类跨入、ZI世纪取得飞速发展的一个不可缺少的重要金属。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种燃烧器用铜合金铸造工艺，生产成本相对较低、导电性能好、抗拉强度高、耐磨损。本专利技术提供的一种燃烧器用铜合金铸造工艺，包括以下步骤：（1）利用感应电炉将铜熔化至熔融状态；（2）在上述液态铜中加入重量相当于铜重量0.45％～0.8％的固体镁；（3）将完全融合的铜镁液态合金浇注成合金铸杆，所需温度控制在1275℃～1485℃之间，铸造速度为1.6～2.4m/h；（4）将合金铸杆快速冷却，冷却水流速为13立方米每小时，进水口温度在19℃～30℃之间，出水口温度在38℃～56℃之间；（5）制得铜合金铸杆。本专利技术提供的一种燃烧器用铜合金铸造工艺，其有益效果在于：铜镁合金使生产成本相对较低，而且合金的熔点比纯金属要低；铜的导电性能好；金属镁增加了合金的硬度，使该铜合金铸杆抗拉强度高、耐磨损。具体实施方式下面结合一个实施例，对本专利技术提供的一种燃烧器用铜合金铸造工艺进行详细的说明。实施例本实施例的一种燃烧器用铜合...
【技术保护点】
一种燃烧器用铜合金铸造工艺，其特征在于：包括以下步骤：（1）利用感应电炉将铜熔化至熔融状态；（2）在上述液态铜中加入重量相当于铜重量0.45％～0.8％的固体镁；（3）将完全融合的铜镁液态合金浇注成合金铸杆，所需温度控制在1275℃～1485℃之间，铸造速度为1.6～2.4m/h；（4）将合金铸杆快速冷却，冷却水流速为13立方米每小时，进水口温度在19℃～30℃之间，出水口温度在38℃～56℃之间；（5）制得铜合金铸杆。
【技术特征摘要】
1.一种燃烧器用铜合金铸造工艺，其特征在于：包括以下步骤：（1）利用感应电炉将铜熔化至熔融状态；（2）在上述液态铜中加入重量相当于铜重量0.45％～0.8％的固体镁；（3）将完全融合的铜镁液态合金浇注成合金铸杆，所...
【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37