The invention discloses a high purity stainless steel gas stove panel preparation method comprises the following steps: melting the raw materials in AOD refining furnace for reductive desulfurization and decarbonization, get molten steel; then conveyed to the ladle; then casting; the process comprises the following steps: AOD refining furnace decarburization end at the same time, investment in ferrosilicon furnace slag desulfurization, desulfurization to S content less than 0.01 wt.%, from the first time in AOD refining furnace tapping to ladle slag in ladle of molten steel, will be re added in the AOD refining furnace and the new slag, slag basicity and oxygen control within a certain range. Then blowing argon stirring furnace from 0.01% to S content in <, from the AOD refining furnace second tapping, get molten steel, the preparation method adopts AOD refining furnace, through double slag process, prevent the hard inclusions produced To produce high purity stainless steel.
【技术实现步骤摘要】
一种燃气灶面板用高纯净不锈钢制备方法
本专利技术属于铸造
，具体涉及一种燃气灶面板用高纯净不锈钢制备方法。
技术介绍
目前，厨具中材质大致有合金、陶瓷、不锈钢等各种材质，其中不锈钢在各方面应用广泛，但随着厨具的发展，不锈钢存在的问题也应运而来，不锈钢中存在硬性夹杂物的时候，在冷轧压延的时候会导致表面缺陷或裂纹，这是由于这些夹杂物在低温下不具有变形能力，在冷轧压延的时候会导致表面缺陷或裂纹，因此，想要获得表面品质良好的高纯净不锈钢冷轧钢卷或钢板，控制连铸坯中的硬性尖晶石(MgO·Al2O3)夹杂物的含量至关重要，如何生产出纯净的不锈钢对我们的生活越来越重要。
技术实现思路
为了克服现有
存在的上述技术问题，本专利技术的目的在于，提供一种燃气灶面板用高纯净不锈钢制备方法，通过控制脱硫工艺和造渣方法，防止产品中出现高熔点的硬性夹杂物，从而制备得到没有表面缺陷的高纯净不锈钢。本专利技术提供的一种燃气灶面板用高纯净不锈钢制备方法，包括以下步骤：1）AOD精炼炉中吹氧脱碳结束后，投入硅铁还原炉渣中氧化铬，同时造渣脱硫，脱硫至炉中S含量＜0.05重量％时，从AOD精炼炉...
【技术保护点】
一种燃气灶面板用高纯净不锈钢制备方法，其特征在于：所述方法包括以下步骤：1）AOD精炼炉中吹氧脱碳结束后，投入硅铁还原炉渣中氧化铬，同时造渣脱硫，脱硫至炉中S含量＜0.05重量％时，从AOD精炼炉中第一次出钢至钢包，在钢包内进行彻底渣，然后将扒渣后的熔钢重新兑入AOD精炼炉中；2)熔钢重新兑入AOD精炼炉后，吹入氧气，吹入氧气量为吨钢8Nm
【技术特征摘要】
1.一种燃气灶面板用高纯净不锈钢制备方法，其特征在于：所述方法包括以下步骤：1）AOD精炼炉中吹氧脱碳结束后，投入硅铁还原炉渣中氧化铬，同时造渣脱硫，脱硫至炉中S含量＜0.05重量％时，从AOD精炼炉中第一次出钢至钢包，在钢包内进行彻底渣，然后将扒渣后的熔钢重新兑入AOD精炼炉中；2)熔钢重新兑入AOD精炼炉后，吹入氧气，吹入氧气量为吨钢8...
【专利技术属性】
技术研发人员：李玉敏，
申请(专利权)人：青岛天地铸造有限公司，
类型：发明
国别省市：山东,37