The invention discloses a composite wood floor, according to the weight of wood flour 60~80, calcium carbonate 10~20, wood lubricant 6~8, terpineol 2~6, sodium carboxymethyl cellulose 2~6, stearic acid 1~2, wood filler impact 0.8 ~ 1, anti UV agents 1~2 copies, 1~2 copies of antioxidants composition. The invention is based on the material adding wood impact filler, wood surface increased flexibility, adhesion to the elastic layer of the floor surface is strong, can increase the floor surface foot comfort, has the function of buffering and noise reduction function, low hardness, not easy to cause in the fall after the human body injury; adding anti UV agent and antioxidant. To avoid the composite floor due to the suction of long mildew, cracking and deformation of the image, improve the service life of the floor.
【技术实现步骤摘要】
一种复合型木地板及其制备方法
本专利技术涉及一种木地板，具体涉及一种复合型木地板及其制备方法。
技术介绍
随着全球天然林资源的急剧减少，木材加工行业出现了原料日益短缺的现象。而木地板作为室内装修的一种重要装饰材料，其市场需求量越来越大，其中三层实木复合地板由于其优良的稳定性和环保性也受到越来越多的国内消费者青睐。传统的木地板一般采用涂装油漆形成表面光滑、硬度较高的保护层以保护木地板，增加木地板的使用寿命，但是表面光滑的木地板容易导致儿童、老人摔倒，而硬度较高的木地板表面在摔倒后极易导致对人体的伤害。目前的复合型地板因吸水而出现长霉、开裂、变形等形象，硬度较高、在摔倒后极易导致对人体的伤害。
技术实现思路
本专利技术的目的在于，提供一种复合型木地板及其制备方法。该专利技术的地板因吸水而不会出现长霉、开裂、变形等形象，硬度较低、在摔倒后不易导致人体的伤害。本专利技术的技术方案：一种复合型木地板，按照重量计，由木粉60～80份，碳酸钙10～20份，木塑润滑剂6～8份，松油醇2～6份、羧甲基纤维素钠2～6份，硬脂酸1～2份，木塑抗冲击填充剂0.8～1份，抗UV助剂1～2份，抗...
【技术保护点】
一种复合型木地板，其特征在于：按照重量计，由木粉60～80份，碳酸钙10～20份，木塑润滑剂6～8份，松油醇2～6份、羧甲基纤维素钠2～6份，硬脂酸1～2份，木塑抗冲击填充剂0.8～1份，抗UV助剂1～2份，抗氧剂1～2份组成。
【技术特征摘要】
1.一种复合型木地板，其特征在于：按照重量计，由木粉60～80份，碳酸钙10～20份，木塑润滑剂6～8份，松油醇2～6份、羧甲基纤维素钠2～6份，硬脂酸1～2份，木塑抗冲击填充剂0.8～1份，抗UV助剂1～2份，抗氧剂1～2份组成。2.根据权利要求1所述的复合型木地板，其特征在于：按照重量计，由木粉70份，碳酸钙15份，木塑润滑剂7份，松油醇4份、羧甲基纤维素钠4份，硬脂酸1.5份，木塑抗冲击填充剂0.9份，抗UV助剂1.5份，抗氧剂1.5份组成。3.一种如权利要求1或2所述的复合型木地板及其...
【专利技术属性】
技术研发人员：贺清华，罗仕香，贺炎辉，
申请(专利权)人：遵义万宝集门木制品有限公司，
类型：发明
国别省市：贵州,52