一种高分子材料专用稳定剂及其制备方法技术

本发明专利技术涉及一种高分子材料专用稳定剂及其制备方法，原料组成成分按重量份数由以下比例组成：硬脂酸钾5‑8份、硬脂酸锉3‑5份、稀土8‑10份、环氧大豆油3‑5份、2一苯基叫噪2‑3份、磺化木质素3‑5份、二苯甲酰甲烷3‑5份、硼酸6‑8份、甘油4‑6份、乙醇20‑30份。本发明专利技术材料易得，稳定效果优良，耐酸耐碱性效果好，透明度高，有效提高机械强度，缩短熔融时间，节约成本，提高工作效率，促进经济效益。

A special stabilizer for polymer material and its preparation method

The invention relates to a special stabilizer polymer material and its preparing method, the compositions of raw materials according to the weight proportion is composed of the following: 5 potassium stearate 8, stearic acid 3 file 5 copies, 10 copies, 8 rare earth epoxy soybean oil 3 5, 2 a 2 phenyl called the noise 3 A, 3 5 sulfonated lignin, two benzoyl methane 3 5 copies, 8 copies, 6 boric acid glycerin 4 6 ethanol, 20 30. The material of the invention is easy to get, stable effect is good, acid and alkali resistance effect is good, transparency is high, mechanical strength is improved effectively, melting time is shortened, cost is saved, work efficiency is improved, and economic benefit is promoted.

【技术实现步骤摘要】
一种高分子材料专用稳定剂及其制备方法
本专利技术涉及一种高分子材料专用稳定剂及其制备方法。
技术介绍
随着社会的发展，稳定剂的发展技术越来越成熟，但就目前市场中高分子材料所用的稳定剂来说，透明度不高，且不能有效改变其材料的缺点，在性能上得不到提高，稳定效果偏差，影响其使用寿命。
技术实现思路
：本专利技术的目的是为了克服以上的不足而提供一种高分子材料专用稳定剂及其制备方法。本专利技术的技术方案包括：一种高分子材料专用稳定剂及其制备方法，原料组成成分按重量份数由以下比例组成：硬脂酸钾5-8份、硬脂酸锉3-5份、稀土8-10份、环氧大豆油3-5份、2一苯基叫噪2-3份、磺化木质素3-5份、二苯甲酰甲烷3-5份、硼酸6-8份、甘油4-6份、乙醇20-30份。本专利技术的进一步改进在于：其制备方法如下：A、将稀土经过高温提纯、超声波分散，温度设为680-720℃，压力为1.5-1.7MPa，冷却后加入2一苯基叫噪和磺化木质素进行搅拌，搅拌速率为520-580r/min，得混合物A；B、将硬脂酸钾和硬脂酸锉和二苯甲酰甲烷进行混合搅拌，加入乙醇中采用超声波溶解，超声频率设为2100-2300HZ，再本文档来自技高网...

【技术保护点】
一种高分子材料专用稳定剂及其制备方法，其特征在于：原料组成成分按重量份数由以下比例组成：硬脂酸钾5‑8份、硬脂酸锉3‑5份、稀土8‑10份、环氧大豆油3‑5份、2一苯基叫噪2‑3份、磺化木质素3‑5份、二苯甲酰甲烷3‑5份、硼酸6‑8份、甘油4‑6份、乙醇20‑30份。

【技术特征摘要】
1.一种高分子材料专用稳定剂及其制备方法，其特征在于：原料组成成分按重量份数由以下比例组成：硬脂酸钾5-8份、硬脂酸锉3-5份、稀土8-10份、环氧大豆油3-5份、2一苯基叫噪2-3份、磺化木质素3-5份、二苯甲酰甲烷3-5份、硼酸6-8份、甘油4-6份、乙醇20-30份。2.根据权利要求1所述的一种高分子材料专用稳定剂及其制备方法，其特征在于：其制备方法如下：A、将稀土经过高温提纯、超声波分散，温度设为6...

【专利技术属性】
技术研发人员：方碧水，
申请(专利权)人：方碧水，
类型：发明
国别省市：安徽,34