本发明专利技术涉及低温塑料领域，公开了一种抗低温的改性塑料，由以下重量份的原料制成：ABS树脂12‑18份、芳族聚碳酸酯树脂16‑26份、PE6‑9份、烷基酚聚氧乙烯醚7‑9份、相容剂SMA树脂7‑10份、纳米硼纤维6‑10份、碳酰二胺12‑19份、碳酸钙5‑8份、偏苯三酸三锌酯6‑10份。本发明专利技术所提供的一种抗低温的改性塑料，提高了塑料在低温环境下的拉伸强度和断裂伸长率，可塑性高，耐冲击，不易脆断。

A modified plastic with low temperature

The invention relates to the field of low temperature plastic, discloses a low temperature resistant modified plastics, made from the following raw materials in weight portion: ABS resin 12 18 copies, 26 copies of 16 aromatic polycarbonate resin, PE6 9, alkyl phenol polyoxyethylene ether 7 9 compatibilizers, SMA resin 10, 7 nano boron fiber 6 10, two 12 carbon acyl amine 19 copies, 8 copies, 5 calcium carbonate trimellitic acid ester 6 10 zinc three. A low temperature resistant modified plastic provided by the invention improves the tensile strength and elongation at break of plastics under low temperature, and has high plasticity, impact resistance and no brittle fracture.

【技术实现步骤摘要】
一种抗低温的改性塑料
本专利技术涉及低温塑料领域，特别是涉及一种抗低温的改性塑料。
技术介绍
塑料，是指以高分子量的合成树脂为主要组分，加入适当添加剂，如增塑剂、稳定剂、阻燃剂、抗菌剂、着色剂等，经加工成型的塑性(柔韧性)材料，或固化交联形成的刚性材料。随着塑料的用途越来越广泛，塑料用品的种类也越来越多。由于塑料自身所展现的诸如质量轻，优良的化学稳定性和电绝缘性及热的不良导体等性能，使塑料的应用领域和地域越来越宽泛。目前使用的塑料制品的使用温度范围比较窄，不能满足需求。在深冷领域、生物领域、食品领域、医药领域会使用到低温液体用于低温处理或保存物品，例如生产中用到的储存液氨用塑料容器、冻存管、冻存架、低温手套等。
技术实现思路
本专利技术旨在提供一种抗低温的改性塑料，以解决现有技术中的上述问题。本专利技术采用的技术方案为：一种抗低温的改性塑料，由以下重量份的原料制成：ABS树脂12-18份、芳族聚碳酸酯树脂16-26份、PE6-9份、烷基酚聚氧乙烯醚7-9份、相容剂SMA树脂7-10份、纳米硼纤维6-10份、碳酰二胺12-19份、碳酸钙5-8份、偏苯三酸三锌酯6-10份。优选的，一种抗低温本文档来自技高网...

【技术保护点】
一种抗低温的改性塑料，其特征在于，由以下重量份的原料制成：ABS树脂12‑18份、芳族聚碳酸酯树脂16‑26份、PE6‑9份、烷基酚聚氧乙烯醚7‑9份、相容剂SMA树脂7‑10份、纳米硼纤维6‑10份、碳酰二胺12‑19份、碳酸钙5‑8份、偏苯三酸三锌酯6‑10份。

【技术特征摘要】
1.一种抗低温的改性塑料，其特征在于，由以下重量份的原料制成：ABS树脂12-18份、芳族聚碳酸酯树脂16-26份、PE6-9份、烷基酚聚氧乙烯醚7-9份、相容剂SMA树脂7-10份、纳米硼纤维6-10份、碳酰二胺12-19份、碳酸钙5-8份、偏苯三酸三...