一种用于降低天线盖板类产品缩痕的注塑工艺制造技术
An injection molding process for reducing the shrinkage mark of the antenna cover plate products
The invention discloses a method for injection molding process to reduce the antenna cover products shrink marks, the corresponding injection molding process and injection mold system is realized based on the melt temperature, the injection molding process is 240 DEG C 250 DEG C, the injection time was 2 5S, the holding time was 10 15s maximum pressure injection pressure peak 120% 140%. The invention relates to an injection molding process for reducing the antenna cover products shrink marks, the maneuverability is strong, easy to implement, and can effectively reduce the shrinkage phenomenon of antenna cover product appearance in the process of injection molding, injection molding products and reduce production cycle, improve production efficiency, reduce production cost.
【技术实现步骤摘要】
一种用于降低天线盖板类产品缩痕的注塑工艺
本专利技术涉及一种用于降低天线盖板类产品缩痕的注塑工艺。
技术介绍
天线盖板类产品常用于通信、信号传输、信号发送等领域，其工作环境特殊，长期暴露于户外、紫外线等全天候的工作环境中，因而要求天线盖板具备耐用、耐恶劣环境等特性。但是，由于注塑材料所固有的性能，再结合天线盖板类产品本身所特有的结构特点（在产品内表面常放置有加强肋板结构），因而在盖板上表面肋板加强处常会有缩痕的出现，由于天线盖板类产品为外观件，故对其外观要求较高。现有技术中对于天线盖板类产品的注塑工艺虽然已有多种，但是始终难以降低天线盖板类产品表面的缩痕现象。
技术实现思路
本专利技术的目的在于提供一种用于降低天线盖板类产品缩痕的注塑工艺，其可操作性强，易于实现，并能有效的降低天线盖板类产品在注塑成型过程中外观的缩痕现象，且减小产品注塑成型的生产周期，提高生产效率，节约生产成本。为实现上述目的，本专利技术的技术方案是设计一种用于降低天线盖板类产品缩痕的注塑工艺，该注塑工艺基于相应的注塑系统和注塑模具来实现，所述注塑工艺的熔料温度为240℃-250℃，注射时间为2-5s...
【技术保护点】
一种用于降低天线盖板类产品缩痕的注塑工艺，该注塑工艺基于相应的注塑系统和注塑模具来实现，其特征在于，所述注塑工艺的熔料温度为240℃‑250℃，注射时间为2‑5s，保压时间为10‑15s，最大保压压力为注射压力峰值的120%‑140%。
【技术特征摘要】
1.一种用于降低天线盖板类产品缩痕的注塑工艺，该注塑工艺基于相应的注塑系统和注塑模具来实现，其特征在于，所述注塑工艺的熔料温度为240℃-250℃，注射时间为2-5s，保压时间为10-15s，最大保压压力为注射压力峰值的120%-140%。2.根据权利要求1所述的用于降低天线盖板类产品缩痕的注塑工艺，其特征在于，所述注塑工艺的熔料温度为240℃，注射时间为3s，保压时间为15s，且保压过程分为两个阶段，第一阶段的保压时间为10s，...
【专利技术属性】
技术研发人员：汪栋，
申请(专利权)人：苏州恒辉科技有限公司，
类型：发明
国别省市：江苏,32