一种带夜光且复合有碳纤维的无纺布制造技术
A nonwoven fabric with noctilucent and composite carbon fiber
The present invention discloses a luminous and composite non-woven fabric of carbon fiber, including the outer layer and inner layer, the outer layer is a luminous layer between the outer layer and the inner layer, intermediate adhesive fiber layer, the inner layer is divided into two layers, the first layer and the second layer; the first layer includes 15 to 35% carbon fiber content and 25 to melt 45% content of melt fiber; the second layer comprises 5 ~ 25% and 35 ~ 55% carbon fiber content of melt hot melt fiber; arranged perpendicular to the direction of the first layer is provided on the fiber orientation and the second layer of the fiber, a mesh structure made of glass fibre is arranged between the first and second layers the screen structure is arranged, the latitude and longitude. The invention relates to a non-woven fabric with a night light and a composite carbon fiber.
【技术实现步骤摘要】
一种带夜光且复合有碳纤维的无纺布
本专利技术涉及一种带夜光且复合有碳纤维的无纺布。
技术介绍
已知一种全部或者由可分割的复合纤维形成、具有微细的纤维的无纺布。但上述无纺布通过非纺织法制造的无纺布会有制造工艺复杂、生产率低的问题，而且成本也会稍高，因此本专利技术设计研发一种新型无纺布，不仅降低成本，而且无纺布的性能也会有一定改进。
技术实现思路
本专利技术涉及一种带夜光且复合有碳纤维的无纺布。为实现这一目的，本专利技术所采用的技术方案是：一种带夜光且复合有碳纤维的无纺布，其特征在于，包括外层和内层，外层为夜光层，外层与内层之间为中间粘合纤维层，中间粘合纤维层由经纱和纬纱绞织而成，所述经纱采用涂覆有聚氨酯层的乙纶纤维，所述纬纱采用涂覆有聚氨酯的锦纶纤维；所述内层为两层结构，分为第一层和第二层；所述第一层包括15～35％含量的碳纤维和25～45％含量的热熔融性纤维；所述第二层包括5～25％碳纤维和35～55％含量的热熔融性纤维；第一层上的纤维排列方向与第二层上的纤维排列方向垂直设置，在第一层和第二层之间还设置有玻璃纤维制成的筛网结构，该筛网结构呈经纬排列。其有益效果是：第一...
【技术保护点】
一种带夜光且复合有碳纤维的无纺布，其特征在于，包括外层和内层，外层为夜光层，外层与内层之间为中间粘合纤维层，中间粘合纤维层由经纱和纬纱绞织而成，所述经纱采用涂覆有聚氨酯层的乙纶纤维，所述纬纱采用涂覆有聚氨酯的锦纶纤维；所述内层为两层结构，分为第一层和第二层；所述第一层包括15～35％含量的碳纤维和25～45％含量的热熔融性纤维；所述第二层包括5～25％碳纤维和35～55％含量的热熔融性纤维；第一层上的纤维排列方向与第二层上的纤维排列方向垂直设置，在第一层和第二层之间还设置有玻璃纤维制成的筛网结构，该筛网结构呈经纬排列。
【技术特征摘要】
1.一种带夜光且复合有碳纤维的无纺布，其特征在于，包括外层和内层，外层为夜光层，外层与内层之间为中间粘合纤维层，中间粘合纤维层由经纱和纬纱绞织而成，所述经纱采用涂覆有聚氨酯层的乙纶纤维，所述纬纱采用涂覆有聚氨酯的锦纶纤维；所述内层为两层结构，分为第一层和第二层；所...
【专利技术属性】
技术研发人员：王平，
申请(专利权)人：天门市畅享生活用品股份有限公司，
类型：发明
国别省市：湖北,42