The present invention relates to the synthesis of acrylamide thermosensitive hydrogels include: weigh 0.5g methylene bis acrylamide and 2.0g ammonium persulfate were prepared in 50mL solution for N, maleoyl N MAGEL0.3 0.5g gelatin dissolved in 40 DEG 7.8mL in deionized water, and then the ice bath in aqueous solutions of gelatin solution in 10 in 3 DEG 10min, adding 0.8 1.2g N N-isopropylacrylamide and crosslinking agent Bis 1.2mL, to be dissolved after filling N2 bubbling 15 30min, initiator TEMED 10 stir after 30min, then added by the initiator APS, rapid stirring 30s, constant temperature tank in 10 C in the static reaction of 24h, deionized water washing products after the product was obtained by freezing dry hydrogel.
【技术实现步骤摘要】
丙烯酰胺温敏性水凝胶的合成
本专利技术涉及丙烯酰胺温敏性水凝胶的合成，属于合成化学领域。
技术介绍
水凝胶是由高分子共价键交联而形成的三维网状结构，是普遍存在于自然界中的一种常见的物质形态。智能水凝胶是一种能够感知周围环境中微小的化学或物理刺激，并做出迅速响应，而且自身的很多性质能够发生明显变化的一类特殊的水凝胶。它能够在水中溶胀吸收大量的水分，但又不溶解于水这与生物机体的许多结构具有相似性，近年来水凝胶已涉及到生物医学、材料科学、农学等诸多领域，许多研究人员对水凝胶的合成、性质以及实际应用进行了广泛的研究。经过近几年来的研究发现，天然高分子化合物如明胶、壳聚糖等，不仅来源丰富，而且具有非常好的生物相容性和可降解性，并且能够通过各种方式引入水凝胶体系中，极大地弥补了传统职能水凝胶细胞毒性大、难降解的缺点。天然高分子化合物的引入进一步打开了智能水凝胶在医药生物领域高速发展的大门，并被广泛应用于水凝胶的制备和性质研究当中。明胶是一种可以再生的天然高分子物质，它以胶原蛋白的形式存在于生物体中。胶原蛋白在高温、强酸、强碱等条件下，容易变性转化为明胶。由于明胶能够通过胶原蛋...
【技术保护点】
丙烯酰胺温敏性水凝胶的合成，其特征在于，包括：准确称取0.5g甲叉双丙烯酰胺和2.0g过硫酸铵分别配成50mL溶液待用，将N‑马来酰化明胶N‑MAGEL0.3‑0.5g溶于40℃的7.8mL去离子水中，然后将明胶溶液置于10℃以下的水溶液中冰浴3‑10min，加入0.8‑1.2g N‑异丙基丙烯酰胺和交联剂Bis 1.2mL，待溶解后充入N2鼓泡15‑30min，加入引发剂TEMED充分搅拌10‑30min后，再加入促引发剂APS，快速搅拌30s，置于10℃的恒温槽中静置反应24h，用去离子水洗涤产物后将产物冷冻干燥得到水凝胶。
【技术特征摘要】
1.丙烯酰胺温敏性水凝胶的合成，其特征在于，包括：准确称取0.5g甲叉双丙烯酰胺和2.0g过硫酸铵分别配成50mL溶液待用，将N-马来酰化明胶N-MAGEL0.3-0.5g溶于40℃的7.8mL去离子水中，然后将明胶溶液置于10℃以下的水溶液中冰浴3-10min，加入0.8-1.2gN-异丙基丙烯酰...
【专利技术属性】
技术研发人员：赵世芬，
申请(专利权)人：烟台智本知识产权运营管理有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。