A steel fiber reinforced concrete and its preparation method relate to the field of building materials. The steel fiber concrete is doped with steel fiber, marble powder and fly ash in concrete system mainly composed of cement, sand and gravel. The formula of the steel fiber concrete is reasonable, can be used for the reuse of industrial waste materials such as marble powder, fly ash and other industrial waste, and turn waste into treasure and reduce production cost. At the same time, through the synergy of each component in the formula, the overall strength of the concrete is improved effectively, and it has high practical value. The preparation method of the steel fiber reinforced concrete is simple, the requirement of the equipment is low, and the steel fiber concrete can be obtained by simple mixing. The cost of production is suitable for large-scale production of industrialization.
【技术实现步骤摘要】
一种钢纤维混凝土及其制备方法
本专利技术涉及建筑材料领域，具体而言，涉及一种钢纤维混凝土及其制备方法。
技术介绍
混凝土是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常讲的混凝土一词是指用水泥作胶凝材料，砂、石作集料与水按一定比例配合，经搅拌而得的水泥混凝土，也称普通混凝土，它广泛应用于土木工程。石粉是石材加工过程中产生的废料，随意排放不仅造成资源的浪费，还会造成环境的污染。将石粉作为混凝土中的掺杂物，不仅可以降低商品混凝土的成本，还可变废为宝，进行资源回收，有效解决我省石材加工企业每年产生数量巨大的石粉利用问题，具有良好的社会效益。目前的相关主要集中在具有一定凝胶活性的石灰石粉上，而对于低活性的大理石粉的研究相对较少。
技术实现思路
本专利技术的目的在于提供一种钢纤维混凝土，其能够对大理石粉加以利用，变废为宝，降低混凝土的整体成本，并且其强度高，具有较高的应用价值。本专利技术的另一目的在于提供一种钢纤维混凝土的制备方法，其操作简单，对设备要求低，生产成本低，适合工业化的大规模生产。本专利技术的实施例是这样实现的：一种钢纤维混凝土，按照重量份数计，其原料包括：...
【技术保护点】
一种钢纤维混凝土，其特征在于，按照重量份数计，其原料包括：水泥30～50份，砂60～80份，碎石70～100份，钢纤维5～10份，大理石粉5～10份，粉煤灰3～5份，水10～20份，减水剂0.5～1份。
【技术特征摘要】
1.一种钢纤维混凝土，其特征在于，按照重量份数计，其原料包括：水泥30～50份，砂60～80份，碎石70～100份，钢纤维5～10份，大理石粉5～10份，粉煤灰3～5份，水10～20份，减水剂0.5～1份。2.根据权利要求1所述的钢纤维混凝土，其特征在于，按照重量份数计，其原料包括：所述水泥35～45份，所述砂60～70份，所述碎石70～85份，所述钢纤维5～8份，所述大理石粉5～8份，所述粉煤灰3～5份，所述水10～20份，所述减水剂0.5～1份。3.根据权利要求1所述的钢纤维混凝土，其特征在于，所述水泥为水硬性胶凝材料；优选地，所述水泥为铝酸盐水泥或硅酸盐水泥。4.根据权利要求1所述的钢纤维混凝土，其特征在于，所述钢纤维的长度为30～60mm，直径为0.5～1mm。5.根据权利要求4所述的钢纤维混凝土，...
【专利技术属性】
技术研发人员：张金团，蔡德所，赵凯月，于冬升，蔡军，王鸣，胡琴，
申请(专利权)人：贺州学院，
类型：发明
国别省市：广西,45