一种柔性导电薄膜制造技术

本发明专利技术公开了一种柔性导电薄膜，以聚氯乙烯树脂为原料，配方还包括纳米银线、间接载体、氧化铁、聚对苯二甲酸丁二醇酯和环氧大豆油，其组分按重量份计分别为：聚氯乙烯树脂60‑75份；纳米银线7‑10份；间接载体20‑25份；氧化铁1‑3份；聚对苯二甲酸丁二醇酯3‑6份；环氧大豆油2‑5份。本发明专利技术的有益效果是：以聚氯乙烯树脂为原料，添加的低密度聚乙烯和环氧大豆油，能增加薄膜的柔软性，同时其它物质的添加，能增强薄膜的耐热性，性能稳定，组分配比科学合理，原料简单易得，满足行业的需求。

A flexible conductive film

The invention discloses a flexible conductive film with polyvinyl chloride resin as raw material, the formulation includes silver nanowires, indirect carrier, iron oxide, polyethylene terephthalate and epoxy soybean oil and its components by weight respectively: 60 PVC resin 75; 7 silver nanowires 10; indirect carrier 20 25 1 3; iron oxide; polybutylene terephthalate 3 6; 2 5 epoxidized soybean oil. The beneficial effects of the invention are: polyvinyl chloride resin as raw material, low density polyethylene and epoxy soybean oil added, can increase the softness of films, and other substances added, can enhance the heat resistance film, stable performance, the distribution ratio is scientific and reasonable, easily available raw materials, to meet the needs of the industry.

【技术实现步骤摘要】
一种柔性导电薄膜
本专利技术涉及一种薄膜，尤其涉及一种柔性导电薄膜。
技术介绍
目前平板显示器制作的需要，自从Badeker报道了通过热蒸发镉使之形成氧化镉透明导电薄膜以来，透明导电薄膜的研究与开发受到普遍重视。上世纪60年代、氧化铟锡成为透明导电膜的主体，之后又发展了金属基复合导电膜、铝掺杂氧化锌薄膜，90年代以来随着光电子产业的发展多组元透明导电氧化物材料、导电高分子膜以及其他透明导电材料应用而生。但是现有的导电薄膜的制备工艺复杂，生产条件苛刻，设备投资过高，同时导电薄膜普遍存在耐热性差的缺点，不能满足需求。因此，为解决上述问题，特提供一种新的技术方案。
技术实现思路
本专利技术提供一种柔性导电薄膜。本专利技术采用的技术方案是：一种柔性导电薄膜，以聚氯乙烯树脂为原料，配方还包括纳米银线、间接载体、氧化铁、聚对苯二甲酸丁二醇酯和环氧大豆油，其组分按重量份计分别为：优选地，所述间接载体为低密度聚乙烯。优选地，所述纳米银线由丙三醇、硝酸银和氯化铵混合制得，所述丙三醇、硝酸银、氯化铵的重量比为2:1:1。本专利技术的有益效果是：以聚氯乙烯树脂为原料，添加的低密度聚乙烯和环氧大豆油，能增加薄膜本文档来自技高网...

【技术保护点】
一种柔性导电薄膜，其特征在于：以聚氯乙烯树脂为原料，配方还包括纳米银线、间接载体、氧化铁、聚对苯二甲酸丁二醇酯和环氧大豆油，其组分按重量份计分别为：

【技术特征摘要】
1.一种柔性导电薄膜，其特征在于：以聚氯乙烯树脂为原料，配方还包括纳米银线、间接载体、氧化铁、聚对苯二甲酸丁二醇酯和环氧大豆油，其组分按重量份计分别为：2.根据权利要求1所述的一种柔性导电薄...

【专利技术属性】
技术研发人员：郑国毜，
申请(专利权)人：太仓佩利斯高分子材料有限公司，
类型：发明
国别省市：江苏,32