The invention discloses a self healing asphalt and a preparation method. It is made from asphalt, organic hydrotalcite, carbon black and vegetable oil by melt blending. The percentage of raw materials is 89% to 95% of bitumen, 3% to 5% of organic talc, 1% to 3% of carbon black and 1% to 3% of vegetable oil. Small size organic LDHs easily uniformly dispersed in asphalt, and the lamellar structure has excellent barrier and shielding effect of heat, oxygen and ultraviolet light, to prevent the asphalt aging and brittle; anti ultraviolet oxidation carbon black with light absorbing high, light energy can be converted into heat energy, thereby effectively to prevent the asphalt produced by ultraviolet radiation aging and degradation. Plant oil can supplement the lost light components in the asphalt aging process, and give the asphalt a good capillary flow performance.
【技术实现步骤摘要】
一种自愈合沥青及其制备方法
本专利技术属于道路工程
，具体涉及一种自愈合沥青及其制备方法。
技术介绍
沥青是一种自愈合材料，在温度较高时，沥青在毛细管力的作用下自发地向微裂纹流动，导致裂纹自愈合。在荷载间歇期，沥青的自愈合能够使沥青路面的模量和强度得到(部分)恢复，疲劳寿命得到延长。然而，沥青混合料在拌合、摊铺、压实和服役过程中会发生热氧老化和紫外老化，导致沥青变硬、毛细管流动能力逐渐降低，从而失去裂纹自愈合性能，大大影响了沥青路面的使用性能，缩短了其使用寿命。利用抗老化和软化剂对沥青进行改性能够延缓沥青变硬变脆，从而使沥青保持良好的毛细管流动能力，是改善沥青自愈合性能的有效途经。掺入普通水滑石和炭黑在一定程度上能够提高沥青的耐老化和自愈合性能，但会使沥青变硬、路用性能有所下降，且水滑石和炭黑等无机粒子与沥青相容性差，导致改性沥青存储稳定性不良。
技术实现思路
本专利技术目的在于针对现有技术的不足，提供一种自愈合沥青及其制备方法，该沥青老化后仍具有良好的毛细管流动能力和优良的自愈合性能。为了实现上述目的，本专利技术的技术方案如下：一种自愈合沥青，由沥青、有机水滑...
【技术保护点】
一种自愈合沥青，其特征在于由沥青、有机水滑石、炭黑和植物油经熔融共混制备而成，其特征在于各原料组成的质量百分比为：沥青89％～95％，有机水滑石3％～5％，炭黑1％～3％，植物油1％～3％。
【技术特征摘要】
1.一种自愈合沥青，其特征在于由沥青、有机水滑石、炭黑和植物油经熔融共混制备而成，其特征在于各原料组成的质量百分比为：沥青89％～95％，有机水滑石3％～5％，炭黑1％～3％，植物油1％～3％。2.如权利要求1所述自愈合沥青，其特征在于所述的有机水滑石为镁铝比3:1的硬脂酸纳改性水滑石，其细度为2500～3500目。3.如权利要求1所述自愈合沥青，其特征在于所述炭黑为抗紫外线抗氧化炭黑，其比表面积为2000～3000m2/g。4.如权利要求1所述自愈合沥青，其特征在于...
【专利技术属性】
技术研发人员：刘全涛，汪曾峰，吴少鹏，陈美祝，李元元，李斌，方昊，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北,42