The invention discloses a sealing plate for sealing non asbestos latex, which belongs to the technical field of sealing materials. By weight, followed in 18~25 samples of aramid fiber, 15~20 hybrid plant fiber, 5~8 aluminum sulfate, 4~8 nano powder mixture, 10~15 latex, 5~10 metal fiber, 8~13 graphite oxide, 5~7 copies and 3~5 copies of casein borax, the aramid fiber and plant fiber mixed and mixed. Then add latex, aluminum sulfate, nano powder mixture, metal fiber, graphite oxide, casein and borax, stirring and mixing, was blank, the blank sheet joining sheet machine, sealing board with asbestos free latex sealing. The seal without asbestos latex prepared by the invention has excellent tensile strength and creep resistance, and also has high compression and resilience.
【技术实现步骤摘要】
一种密封用无石棉胶乳抄取板
本专利技术公开了一种密封用无石棉胶乳抄取板，属于密封材料
技术介绍
封材料广泛应用于石油、化工、机械等行业。长期以来，石棉类密封材料因具有耐化学腐蚀、抗热、阻燃、加工容易及成本低等独特优点，一直是密封材料领域的主要组成部分。但石棉纤维在制造加工和使用过程中都会对人体健康造成很大伤害，随着对石棉危害性的认同，采用新型无石棉密封材料替代传统石棉密封材料已成为密封材料领域近年来最显著的变化。非石棉胶乳抄取板（简称无石棉胶乳板）是一种重要的密封材料，主要用于汽车、飞机、摩托车发动机以及各种管道连接的密封等，其主要组分为非石棉纤维、胶乳（或橡胶）粘接剂、各种补强与增容性填料及少量化学助剂复合而成，最终产品要求具有较高的机械强度，良好的压缩回弹性能、较好的密封性能以及优异的抗介质性。由于非石棉纤维种类繁多，不同的非石棉纤维和密封材料的特殊性能要求导致无石棉密封材料配方的多样化，通常包含5%～20%的有机纤维（或浆粕）、10%～20%的弹性粘接剂，剩下大部分是一种或两种填料（或无机非石棉纤维）及少量化学助剂。非石棉胶乳抄取板制造方法是首先通...
【技术保护点】
一种密封用无石棉胶乳抄取板，其特征在于：是由以下重量份数的原料组成：芳纶 18～25份混合植物纤维浆料 15～20份硫酸铝 5～8份纳米粉末混合液 4～8份胶乳 10～15份金属纤维 5～10份氧化石墨 8～13份酪素 5～7份硼砂 3～5份所述混合植物纤维的制备方法为：将漂白针叶木浆与阔叶桉木浆按质量比2：1～3：1混合，并加入针叶木浆质量0.1～0.3倍的沼液，恒温发酵，得混合植物纤维浆料；所述纳米粉末混合液的制备方法为...
【技术特征摘要】
1.一种密封用无石棉胶乳抄取板，其特征在于：是由以下重量份数的原料组成：芳纶18～25份混合植物纤维浆料15～20份硫酸铝5～8份纳米粉末混合液4～8份胶乳10～15份金属纤维5～10份氧化石墨8～13份酪素5～7份硼砂3～5份所述混合植物纤维的制备方法为：将漂白针叶木浆与阔叶桉木浆按质量比2：1～3：1混合，并加入针叶木浆质量0.1～0.3倍的沼液，恒温发酵，得混合植物纤维浆料；所述纳米粉末混合液的制备方法为：将纳米二氧化硅与纳米二氧化钛按质量比2：1～4：1混合，并加入纳米二氧化硅质量5～6倍的水，纳米二氧化硅质量0.1～0.4倍的分散剂和纳米二氧化硅质量0.4～0.8倍的硅烷偶联剂KH-560，搅拌混合，得纳米粉末混合液；所述密封用无石棉胶乳抄取板的制备方法为：（1）按原料组成称量各组分；（2）将芳纶与混合植...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。