The invention discloses a method for preparing calcium carbonate a special coating, based on calcium carbonate prepared by traditional methods, one is the part of the shell powder calcination of calcium carbonate, calcium carbonate, calcium carbonate, which compared to the traditional structure, a hole shape, with adsorption ability is very good, and the cost is the two is not high; the further addition of sodium silicate can significantly improve the coating gloss and mechanical strength, three is the addition of poly naphthalene formaldehyde sodium sulfonate as dispersing agent, can significantly improve the dispersion effect of sodium silicate in preparation method of special heavy calcium carbonate coating of the invention, not only control the cost, but also significantly to improve the properties of subsequent prepared paint, is a preparation method of environmental protection and safety of heavy calcium carbonate.
【技术实现步骤摘要】
一种涂料专用重质碳酸钙的制备方法
本专利技术涉及碳酸钙制备
，尤其是涉及一种涂料专用重质碳酸钙的制备方法。
技术介绍
碳酸钙是一种无机化合物，俗称：灰石、石灰石、石粉、大理石等。主要成分：方解石，化学式是CaCO3，呈中性，基本上不溶于水，溶于盐酸。它是地球上常见物质，存在于霰石、方解石、白垩、石灰岩、大理石、石灰华等岩石内，亦为动物骨骼或外壳的主要成分。碳酸钙是重要的建筑材料，工业上用途甚广。碳酸钙是由钙离子和碳酸根离子结合生成的，所以既是钙盐也是碳酸盐。根据碳酸钙生产方法的不同，一般可以将碳酸钙分为重质碳酸钙和轻质碳酸钙。重质碳酸钙是用机械方法(用雷蒙磨或其它高压磨)直接粉碎天然的方解石、石灰石、白垩、贝壳等就可以制得。由于重质碳酸钙的沉降体积比轻质碳酸钙的沉降体积小，所以称之为重质碳酸钙。性质：白色粉末。无臭、无味。露置空气中无变化，比重2.710。熔点1339℃。几乎不溶于水在含有铵盐或三氧化二铁的水中溶解，不溶于醇。遇稀醋酸、稀盐酸、稀硝酸发生泡沸，并溶解。加热分解为氧化钙(CaO)和二氧化碳(CO2)。轻质碳酸钙又称沉淀碳酸钙，简称轻钙，是将石灰...
【技术保护点】
一种涂料专用重质碳酸钙的制备方法，其特征在于，包括以下步骤：A、将石灰石粉碎后在900‑1200℃煅烧2‑4h得到氢氧化钙，并将贝壳在700‑800℃煅烧5‑8h并粉碎得到贝壳粉；B、将步骤A所得氢氧化钙与水进行连续消化；并陈化3‑8小时，C、将氢氧化钙置入碳化塔进行碳化作业，得到pH为6.8‑7.5的碳酸钙；D、所得碳酸钙过碳化并加入贝壳粉，得到混合浆液；E、所得混合浆液去除杂质，得到碳酸钙精浆；F、加入硅酸钠和聚萘甲醛磺酸钠盐，搅拌均匀后脱水，即可。
【技术特征摘要】
1.一种涂料专用重质碳酸钙的制备方法，其特征在于，包括以下步骤：A、将石灰石粉碎后在900-1200℃煅烧2-4h得到氢氧化钙，并将贝壳在700-800℃煅烧5-8h并粉碎得到贝壳粉；B、将步骤A所得氢氧化钙与水进行连续消化；并陈化3-8小时，C、将氢氧化钙置入碳化塔进行碳化作业，得到pH为6.8-7.5的碳酸钙；D、所得碳酸钙过碳化并加入贝壳粉，得到混合浆液；E、所得混合浆液去除杂质，得到碳酸钙精浆；F、加入硅酸钠和聚萘甲醛...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。