BDO类无毒塑化剂及其制备方法技术

本发明专利技术提供了BDO类无毒塑化剂及其制备方法，所述BDO类无毒塑化剂可替代邻苯二甲酸酯(欧美已禁用)，解决国内BDO过剩的局面，延伸产业链条，增强企业的抗风险能力；制备方法方面，由于酯化反应属于微放热反应，升高温度对反应不利，但温度过低，反应速率过慢，本申请通过对于反应温度以及催化剂的特定选取，加快反应速率，缩短反应时间，简化后处理工序，高效完成酯化反应。

BDO nontoxic plasticizer and its preparation method

The present invention provides a BDO class of non-toxic plasticizer and preparation method thereof, wherein BDO nontoxic plasticizer can replace phthalic acid esters (two European disabled), to solve the domestic situation of excess BDO, extend the industrial chain, enhance the anti risk ability of enterprises; the preparation method, the esterification reaction belongs to micro exothermic reaction. Elevated temperature on adverse reactions, but the temperature is too low, the reaction rate is too slow, the application through the specific selection of reaction temperature and catalyst, the reaction rate, shorten reaction time, simplify postprocessing procedures, efficient completion of the esterification reaction.

【技术实现步骤摘要】
BDO类无毒塑化剂及其制备方法
本专利技术涉及增塑剂生产领域，尤其是BDO类无毒塑化剂及其制备方法。
技术介绍
增塑剂是一种“类溶剂”的物质。加入到塑料、树脂或弹性体等物质中时能改进它们的加工性能，增加可塑性、柔韧性、拉伸性或膨胀性的物质。加入增塑剂可以降低塑料的熔融黏度、玻璃化温度和弹性体的弹性模量，而不会改变被增塑性物质的化学性质。因此可根据工艺加工要求广泛用于塑料生产和塑料制品加工。国内BDO装置，自2014年以来，因国际原油价格暴跌导致化工产品价格长期低位运行，装置运行经济效益较差。作为主流塑化剂的邻苯二甲酸酯在欧美等国被禁止使用后，国内生产企业纷纷寻找新型无毒代用品。
技术实现思路
本专利技术所要解决的技术问题在于提供一种BDO类无毒塑化剂。本专利技术所要解决的另一技术问题在于提供上述BDO类无毒塑化剂的制备方法。为解决上述技术问题，本专利技术的技术方案是：一种BDO类无毒塑化剂，为1,4-丁二醇(BDO)二苯甲酸酯塑化剂，具有(Ⅰ)所示结构：上述BDO类无毒塑化剂的制备方法，具体步骤如下：向搅拌釜式反应器内依次加入每苯甲酸10～20mol、BDO3～10mol、罗门哈斯强酸性本文档来自技高网...

【技术保护点】
一种BDO类无毒塑化剂，其特征在于：为1,4‑丁二醇二苯甲酸酯塑化剂，具有(Ⅰ)所示结构：

【技术特征摘要】
1.一种BDO类无毒塑化剂，其特征在于：为1,4-丁二醇二苯甲酸酯塑化剂，具有(Ⅰ)所示结构：2.权利要求1所述BDO类无毒塑化剂的制备方法，其特征在于：具体步骤如下：向搅拌釜式反应器内依次加入每苯甲酸10～20mol、BDO3～10mol、罗门哈斯强酸性阳离子树脂1～10g，然后密封反应釜，打开搅拌、真空泵以及外部...