一种环氧树脂用高效阻燃剂分散液及其制备方法技术
A high efficiency flame retardant dispersing solution for epoxy resin and its preparation method
The invention relates to a flame retardant epoxy resin with high dispersion and preparation method thereof, liquid by graphite oxide dispersed in a solvent and then mixed with phosphorus azine compounds to obtain the efficient flame retardant composite dispersant; the phospha azine compounds 5,10 two hydrogen phospha azine 10 oxide and its derivatives. Epoxy resin provided by the invention with high dispersion and flame retardant epoxy resin prepolymer mixing temperature is low, in smaller dosage conditions has excellent flame retardant effect to epoxy resin (2.5 phr in the cured epoxy resin by UL 94 V 0 grade), and not effect of epoxy resin and even improve the mechanical strength and thermal stability.
【技术实现步骤摘要】
一种环氧树脂用高效阻燃剂分散液及其制备方法
本专利技术涉及阻燃剂
，具体涉及一种适用于环氧树脂的高效阻燃剂分散液及其制备方法。
技术介绍
双酚A型环氧树脂(通称环氧树脂)具有优异的粘接性、电气绝缘性、耐化学品性、较高的拉伸强度、良好的制品尺寸稳定性等优点，被广泛用作胶黏剂、耐腐涂料、绝缘材料、层压材料等，直接或间接地几乎遍及所有工业领域，但高度的易燃性使其在应用过程中存在巨大的安全隐患。加入阻燃剂可以赋予环氧树脂一定的阻燃性，无卤阻燃是当前的发展方向，其中磷系阻燃剂因具有较高的阻燃效率获得广泛关注，如目前9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)及其衍生物较多地应用于环氧树脂的阻燃，但其质量用量较高，常引起环氧树脂力学性能和热学性能明显下降。最近华南理工大学的QinqinLuo等(RSCAdvances,2015,5:68476–68484)发现5,10-二氢-磷杂吖嗪-10-氧化物(DPPA)及其衍生物用于环氧树脂的阻燃有很好的效果，添加3.2份的DPPA即可使环氧树脂固化物通过UL94V-0等级，但即使在如此低的用量下，该类化合物的...
【技术保护点】
一种环氧树脂用高效阻燃剂分散液，其特征在于：所述高效阻燃剂分散液由氧化石墨分散于溶剂后再与磷杂吖嗪类化合物复合得到；所述磷杂吖嗪类化合物为DPPA、H‑DPPA、HD‑DPPA、HB‑DPPA中的一种。
【技术特征摘要】
1.一种环氧树脂用高效阻燃剂分散液，其特征在于：所述高效阻燃剂分散液由氧化石墨分散于溶剂后再与磷杂吖嗪类化合物复合得到；所述磷杂吖嗪类化合物为DPPA、H-DPPA、HD-DPPA、HB-DPPA中的一种。2.根据权利要求1所述的环氧树脂用高效阻燃剂分散液，其特征在于：所述溶剂为无水乙醇或甲醇，所述氧化石墨与溶剂质量比为1：50～60。3.根据权利要求1所述的环氧树脂用高效阻燃剂分散液，其特征在于：所述氧化石墨与磷杂吖嗪类化合物质量比为1：8～12。4.一种权利要求1-3任一所述的环氧树脂用高效阻燃剂分散液的制备方法，其特征在于步骤如下：将氧化石墨和溶剂混合，搅拌均匀后加入磷杂吖嗪类化合物，继续搅拌1～2h后进行超声分散处理，然后在60～80℃下搅拌反应5～6h，得到环氧树脂用高效阻燃剂分散液。5.根据权利要求4所述的制备方法，其特征在于所述超声分散处理工艺条件为：超声功率为300～400W，超声时间为10～30min。6.一种含有权利要求1-3任一所...
【专利技术属性】
技术研发人员：范国强，张敏，黄晓明，
申请(专利权)人：广州埃米石墨烯投资管理有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。