The invention discloses a flame retardant plastic crafts, flame retardant plastic products, which is characterized in that the water soluble polyamide resin 70, mica powder 14, talcum powder 7, calcium carbonate 12, wollastonite 9 copies, 27 copies of the waterborne epoxy resin emulsion and silica aerogel particles 6 a nano hollow ceramic beads 11, dispersant 2, thickening agent 3, film-forming agent, leveling agent 0.9 copies 0.6 copies and 13 copies of water, the water was deionized water. By applying the application of the flame retardant to the surface of the plastic handicraft, it has good thermal insulation performance, and the surface of the plastic handicraft will not be deformed at high temperature.
【技术实现步骤摘要】
一种用于塑料工艺品的阻燃剂及其制备方法
本专利技术涉及阻燃剂
，具体地，涉及一种用于塑料工艺品的阻燃剂及其制备方法。
技术介绍
目前，大量工艺品摆饰由塑料注塑成型，从而具有防摔坏的性能。然而，塑料制品具有易燃性，存在安全隐患，特别对于一些具有收藏价值的摆饰，如若烧损则损失较大。
技术实现思路
针对现有技术的不足，本专利技术提供一种双组分丙烯酸聚氨酯光油及其制备方法。本专利技术公开的一种用于塑料工艺品的阻燃剂，用于塑料工艺品的阻燃剂，其特征在于，包括水溶性聚酰胺树脂70份、云母粉14份、滑石粉7份、碳酸钙12份、硅灰石9份、水性环氧乳液27份、二氧化硅气凝胶颗粒6份、纳米空心陶瓷微珠11份、分散剂2分、增稠剂3份、成膜助剂0.9份、流平剂0.6份和水13份。根据本申请的一实施方式，水为去离子水。与现有技术相比，本专利技术可以获得包括以下技术效果：通过将本申请的阻燃剂涂覆于塑料工艺品表面，具有良好的隔热性能，塑料工艺品的表面在高温状态下不会出现变形的状况。具体实施方式以下将揭露本申请的多个实施方式，为明确说明起见，许多实务上的细节将在以下叙述中一并说明。然而，应了解...
【技术保护点】
一种用于塑料工艺品的阻燃剂，其特征在于，包括水溶性聚酰胺树脂70份、云母粉14份、滑石粉7份、碳酸钙12份、硅灰石9份、水性环氧乳液27份、二氧化硅气凝胶颗粒6份、纳米空心陶瓷微珠11份、分散剂2分、增稠剂3份、成膜助剂0.9份、流平剂0.6份和水13份。
【技术特征摘要】
1.一种用于塑料工艺品的阻燃剂，其特征在于，包括水溶性聚酰胺树脂70份、云母粉14份、滑石粉7份、碳酸钙12份、硅灰石9份、水性环氧乳液27份、二氧化硅气凝胶颗粒6份...