The invention discloses a damping block and its production method, including the following parts: the quality of butyl rubber 20~25, 20~25 recycled rubber, paraffin oil, polyisobutylene, 10~15 12~15 barium sulfate 18~24, iron oxide powder 1.5 ~ 2, 0.6 ~ 0.9. Its production methods are: 1) medium temperature pyrolysis, 2) mixing, 3) extrusion molding, 4) cutting and 5) packing. The invention has the advantages of simple process, obvious economic benefits, not only reduces the manufacturing cost of the damping block, simplifies the process steps, and damping block are more stable and reliable performance, improve internal damping block compactness, the section thickness of damping block is more uniform, improve production efficiency.
【技术实现步骤摘要】
一种阻尼块及其生产方法
本专利技术涉及一种阻尼块及其生产方法。
技术介绍
随着社会不断进步和发展，振动和噪声出现的频率和场所越来越多，振动、冲击、噪声对社会生产和社会生活产生了严重的危害，振动、噪声污染已成为与水污染和大气污染相提并论的世界三大污染之一。因此，减振降噪是当前环境保护迫切需要解决的重要问题之一。采用阻尼材料是解决上述问题的一种有效手段，聚合物具有弹性，由分子链运动产生内摩擦，将吸收的机械能和声能转化为热能消耗。但是现有的阻尼材料中一般都添加有碳黑，碳黑质量轻、易四处飞扬，污染环境和危害操作人员健康，同时增加了阻尼材料的制造成本，而且现有技术中的阻尼材料性能不稳定，阻尼材料的内部密实度不高，使用寿命大大降低。
技术实现思路
本专利技术目的在于针对现有技术所存在的不足而提供一种阻尼块及其生产方法的技术方案，不仅降低了阻尼块的制造成本，简化了工艺步骤，而且得到的阻尼块性能更稳定可靠，提高阻尼块内部的密实度，使阻尼块的断面厚度更均匀，提高了生产效率。为了解决上述技术问题，本专利技术采用如下技术方案：一种阻尼块，其特征在于包括如下质量份：丁基橡胶20～25份、再生...
【技术保护点】
一种阻尼块，其特征在于包括如下质量份：丁基橡胶20～25份、再生橡胶20～25份、石蜡机油10～15份、聚异丁烯12～15份、硫酸钡18～24份、氧化铁粉1.5～2.0份、防老剂0.6～0.9份。
【技术特征摘要】
1.一种阻尼块，其特征在于包括如下质量份：丁基橡胶20～25份、再生橡胶20～25份、石蜡机油10～15份、聚异丁烯12～15份、硫酸钡18～24份、氧化铁粉1.5～2.0份、防老剂0.6～0.9份。2.根据权利要求1所述的一种阻尼块，其特征在于：所述防老剂为N-苯-α-苯胺、N-苯-β-萘胺、N-苯-N’-环己基对苯二胺、N-N’-二苯基-对苯二胺中的一种或一种以上混合物。3.生产如权利要求1所述的一种阻尼块的方法，其特征在于包括如下步骤：1)中温热解首先将丁基橡胶和再生橡胶进行选择和破碎，并将选择和破碎后的物料从顶部加入固定床热解反应器中，控制反应器中的物料与气体界面温度在100～300℃，混合后的物料通过燃烧床向下移动的过程中，从反应器的底部引入预热的空气或氧气，并控制反应温度在600～900℃；2)混炼a、首先将步骤1)中得到物料加入到密炼机中，搅拌均匀后再向密炼机中加入硫酸钡和防老剂，在120～150℃的温度条件下进行混炼；b、再向上述得到的产物中加入石蜡机油、聚异丁烯和氧化铁粉，在150～180℃的温度条件下进行二次混炼，70～120秒后进行排胶，并将排胶物料通过开炼机进行出片，得到混炼胶片；...
【专利技术属性】
技术研发人员：邹道毅，陈春君，
申请(专利权)人：青岛开拓隆海制冷配件有限公司，
类型：发明
国别省市：山东,37