The invention belongs to the technical field of clinical medical implants, in particular to a biodegradable iron based cardiovascular stent material and a preparation method. The technical scheme of the invention are as follows: a biodegradable iron based cardiovascular stent materials, composed of iron, manganese and silver powder prepared, mass ratio of iron, manganese and silver powder is 75:23:2, iron powder with purity of 99.99%, purity of manganese powder is 99.99%, the purity of silver is 99.99%. The scaffold material provided by the invention has excellent mechanical properties, biocompatibility, biodegradability and bactericidal ability, and fully meets the requirements of clinical interventional therapy for implants.
【技术实现步骤摘要】
一种可降解铁基心血管支架材料及其制备方法
本专利技术属于临床医学植入体
,具体涉及一种可降解铁基心血管支架材料及其制备方法。
技术介绍
随着社会的不断进步,心血管疾病的发病率逐渐增大,严重危害到人类的身体健康。目前心血管疾病通常采用介入疗法,由于血管支架的植入能够为心血管提供支撑,从而成为治疗心血管疾病最有效的方法之一。临床上不仅希望可降解支架材料与生物体的良好适应性和生物相容性、无毒性,而且要求植入的支架能够在植入后最初的12个月内保持力学性能的完整性,并在之后的12-24个月内完全降解。传统的心血管支架材料一般采用可降解高分子、镁合金、铁基合金等。然而高分子材料不仅在降解过程中容易产生团聚现象,而且其X光显影效果差,不利于跟踪和定位,而镁合金的降解速率过快,不能保持所需的力学性能,因此均难以满足临床医学对可降解心血管支架材料的要求。铁基合金不仅具有优异的力学性能,而且是构成人体的必需微量元素之一,参与氧气的转运,铁离子还是很多酶促反应的辅助因子,直接影响DNA合成以及氧化还原酶的活性,因此铁基可降解材料作为可降解植入物时,其降解产生的铁离子可以被人体吸收参与新陈代谢,不会累积毒性,能够提供足够的安全保障,逐渐引起了临床医学的广泛关注。
技术实现思路
本专利技术提供一种可降解铁基心血管支架材料及其制备方法,该支架材料具有优异力学性能、生物相容性、生物降解性及杀菌能力,完全满足临床医学介入疗法对植入体的要求。本专利技术的技术方案如下:一种可降解铁基心血管支架材料,由铁粉、锰粉和银粉制备而成,铁粉、锰粉和银粉的质量比例为75:23:2,铁粉的纯度为99.9 ...
【技术保护点】
一种可降解铁基心血管支架材料,其特征在于,由铁粉、锰粉和银粉制备而成,铁粉、锰粉和银粉的质量比例为75:23:2,铁粉的纯度为99.99%,锰粉的纯度为99.99%,银粉的纯度为99.99%。
【技术特征摘要】
1.一种可降解铁基心血管支架材料,其特征在于,由铁粉、锰粉和银粉制备而成,铁粉、锰粉和银粉的质量比例为75:23:2,铁粉的纯度为99.99%,锰粉的纯度为99.99%,银粉的纯度为99.99%。2.一种如权利要求1所述的可降解...