Aluminum magnesium alloy wire of the invention discloses a method for applying to the cable, the rare earth element La is added to the aluminum magnesium alloy, thus significantly reduce the hot cracking tendency of alloys, and improve the mechanical properties of the alloy, tensile strength and elongation of alloy significantly improve the removal system in Si and other inorganic elements and adding a small amount of metal Ce can improve the tensile strength and elongation of the alloy; machined aluminum magnesium alloy wire diameter 3.0mm, tensile strength can reach 380MPa, elongation can reach 22%. At the same time, considering the application cost, the addition of rare earth La elements is small and the cost is more economical. The alloy has a wide prospect in the actual industrial production.
【技术实现步骤摘要】
一种应用于电缆的铝镁合金线材及其制备方法
本专利技术涉及金属合金材料制备领域，涉及一种应用于电缆的铝镁合金线材及其制备方法。
技术介绍
我国是电子通信材料的生产和出口大国，长时期以来电子线缆行业所生产的终端产品使用的几乎是纯铜线，为此需要耗用大量的铜资源，而我国铜资源紧缺，铜材料价格也较贵，导致生产成本和终端消费成本增加。而铝镁合金线作为一种新型的可替代纯铜圆线的屏蔽功能材料，是一种新型通信材料，用于同轴电缆等信号传输线的外导体编织线，可广泛应用于信息传输领域，为新兴行业宽带传输网络和通讯网络配套，并应用于军工业和航空航天领域。铝镁合金线通常采用主要的铝锭、镁锭、铬锭等原料进行混合，然后经反射熔炼炉熔炼，平引铸杆，然后采用拉拔—退火—拉拔—退火反复使用的方法拉制各种规格的线材。为提高铝镁合金的机械性能，本专利技术提供了一种应用于电缆的铝镁合金线材及其制备方法。
技术实现思路
本专利技术目的在于通过添加稀土元素La提升合金的综合机械性能。一种应用于电缆的铝镁合金线材，其中各合金组分及其重量百分比为：Cu含量为2.0-3.5％，Mg含量为4.8-8.0％，Ce含量为0.0...
【技术保护点】
一种应用于电缆的铝镁合金线材，其特征在于，其中各合金组分及其重量百分比为：Cu含量为2.0‑3.5%，Mg含量为4.8‑8.0%，Ce含量为0.08‑0.2%，稀土La含量为0.5‑1%，余量为Al。
【技术特征摘要】
1.一种应用于电缆的铝镁合金线材，其特征在于，其中各合金组分及其重量百分比为：Cu含量为2.0-3.5%，Mg含量为4.8-8.0%，Ce含量为0.08-0.2%，稀土La含量为0.5-1%，余量为Al。2.如权利要求1所述的应用于电缆的铝镁合金线材，其特征在于，所述的稀土La的重量百分比优选为0.6-0.8%。3.如权利要求1所述的应用于电缆的铝镁合金线材，其特征在于，所述的铝镁合金中，除以上金属元素外，其它杂质的含量低于0.1%。4.如权利要求3所述的应用于电缆的铝镁合金线材，其特征在于，所述的铝镁合金中Si含量低于0.02%。5.一种应用于电缆的铝镁合金线材的制备方法，其特征在于，包括以...
【专利技术属性】