The invention discloses a good wear resistance of Teflon engineering plastics, including PTFE, sodium bicarbonate, chloride two tetrafluoroethane, polyamide, talc, titanium dioxide, calcium stearate, fluorescent whitening agent, engineering plastics were the Teflon resistance points accounted for some proportion by weight: 95 to 105, PTFE 2, 7, two sodium chloride 11 tetrafluoroethane 18, talcum powder 5 10 copies, 22 copies, polyamide 16 titanium dioxide 17 24 copies, 6 copies, 1 calcium fluorescent whitening agent 2 8. By the way, the good wear resistance of Teflon plastic, even after a long time the friction of foreign goods, can still maintain very good properties, not broken damage phenomenon, high or low temperature conditions have no effect on wear resistance.
【技术实现步骤摘要】
一种耐磨性能好的特氟龙工程塑料
本专利技术涉及塑料领域，特别是涉及一种耐磨性能好的特氟龙工程塑料。
技术介绍
特氟龙，英文名称为Polytetrafluoroethylene，英文缩写为PTFE。特氟龙材料的产品一般统称作不粘涂层，是一种使用了氟取代聚乙烯中所有氢原子的人工合成高分子材料。这种材料具有抗酸抗碱、抗各种有机溶剂的特点，几乎不溶于所有的溶剂。同时，特氟龙具有耐高温的特点，它的摩擦系数极低，所以可作润滑作用之途，亦成为了不沾锅和水管内层的理想涂料。现有的工程塑料比较脆，使用后长时间磨下就会坏掉，影响使用。
技术实现思路
本专利技术主要解决的技术问题是提供一种耐磨性能好的特氟龙工程塑料，使用效果好。为解决上述技术问题，本专利技术采用的一个技术方案是：提供一种耐磨性能好的特氟龙工程塑料，包括聚四氟乙烯、碳酸氢钠、二氯四氟乙烷、滑石粉、聚酰胺、二氧化钛、硬脂酸钙、荧光增白剂，所述耐磨性能好的特氟龙工程塑料各组分占有的比例为：以重量份计，聚四氟乙烯95-105份、碳酸氢钠2-7份、二氯四氟乙烷11-18份、滑石粉5-10份、聚酰胺16-22份、二氧化钛17-24份、...
【技术保护点】
一种耐磨性能好的特氟龙工程塑料，其特征在于，包括聚四氟乙烯、碳酸氢钠、二氯四氟乙烷、滑石粉、聚酰胺、二氧化钛、硬脂酸钙、荧光增白剂，所述耐磨性能好的特氟龙工程塑料各组分占有的比例为：以重量份计，聚四氟乙烯 95‑105份、碳酸氢钠 2‑7份、二氯四氟乙烷 11‑18份、滑石粉 5‑10份、聚酰胺 16‑22份、二氧化钛 17‑24份、硬脂酸钙 1‑6份、荧光增白剂 2‑8份。
【技术特征摘要】
1.一种耐磨性能好的特氟龙工程塑料，其特征在于，包括聚四氟乙烯、碳酸氢钠、二氯四氟乙烷、滑石粉、聚酰胺、二氧化钛、硬脂酸钙、荧光增白剂，所述耐磨性能好的特氟龙工程塑料各组分占有的比例为：以重量份计，聚四氟乙烯95-105份、碳酸氢钠2-7份、二氯四氟乙烷11-18份、滑石粉5-10份、聚酰胺16-22份、二氧化钛17-24份、硬脂酸钙1-6份、荧光增白剂2-8份。2.根据权利要求1所述的耐磨性能好的特氟龙工程塑料，其特征在于，所述耐磨性能好的特氟龙工程塑料各组分占有的比例为：以重量份计，聚四氟乙烯95份、碳酸氢钠7份、二氯四氟乙烷11份、滑石粉10份、聚酰胺16份、二氧化钛24份、硬脂酸钙1份、荧光增白剂8份。3.根据权利要求1所述的耐磨性能好的特氟龙工程塑料，其特征在于，所述耐磨性能好的特氟龙工程塑料各组分占有的比例为：以重量份计，聚四氟乙烯105份、碳酸氢钠2份、二氯四氟乙烷18份、滑石粉5份、聚...