一种单宁酸改性白炭黑补强丁苯橡胶的制备方法技术

本发明专利技术中提供的一种单宁酸改性白炭黑补强丁苯橡胶的制备方法，包括如下的步骤：将丁苯橡胶和顺丁橡胶置于密炼机内进行密炼，依次加入白炭黑、单宁酸、氧化锌和硬脂酸，混炼均匀后排料，冷却备用；将第一步制得的胶料投入开炼机，完全包辊后加入促进剂、硫黄，吃料完全后割刀，薄通，下片，停放备用。本方法制备的单宁酸改性白炭黑补强丁苯橡胶具有副反应少、生产成本低和硫化胶力学性能好等诸多优点。

Preparation of a tannic acid modified white carbon black styrene butadiene rubber

A preparation method of the invention provides tannic acid modified silica filled styrene butadiene rubber, which comprises the following steps: styrene butadiene rubber and butadiene rubber in the internal mixer for mixing, followed by adding silica, tannic acid, stearic acid and Zinc Oxide, mixing evenly back material, cooling backup glue; the first step was the material into the mill, and after adding completely wrapped accelerator, sulfur, feed completely after cutting knife, thin, sheet, spare parking. The tannic acid modified silica modified styrene butadiene rubber has many advantages, such as less side reaction, low production cost and good mechanical properties of vulcanizate.

【技术实现步骤摘要】
一种单宁酸改性白炭黑补强丁苯橡胶的制备方法
本专利技术涉及一种橡胶制备方法，具体涉及一种单宁酸改性白炭黑补强丁苯橡胶的制备方法。
技术介绍
白炭黑是橡胶行业中使用的一种重要的补强填料，常用在浅色橡胶制品中以替代炭黑进行补强，满足白色或半透明产品的需要；相对于炭黑，白炭黑具有更低的滚动阻力、更强的粘附力、抗撕裂及耐热抗老化性能，所以在黑色橡胶制品中亦可替代部分炭黑，以获得高质量的橡胶制品，如越野轮胎、工程轮胎、子午胎等。但是同炭黑相比，白炭黑的加工性能较差，这个缺点严重的限制了其在橡胶行业中的应用。现有技术中通常使用硅烷偶联剂对白炭黑进行改性，从而提高其与橡胶间的亲和性，提高其在橡胶基体中的分散性，以改善胶料的加工性能，同时提高胶料的定伸应力、拉伸强度、撕裂强度以及耐磨性。但是现有技术中使用的硅烷偶联剂，对湿度比较敏感，与白炭黑间的硅烷化反应程度主要依赖于反应温度，即混炼温度或混炼时排胶温度，副反应产生乙醇等气体导致硫化橡胶产生针孔，对橡胶与金属骨架材料的黏合产生不利影响，从而对硫化橡胶的质量产生不良影响。因此，寻找一种新型的白炭黑改性剂，对于降低副反应，提高白炭黑改性效果，提高硫化橡本文档来自技高网...

【技术保护点】
一种单宁酸改性白炭黑补强丁苯橡胶的制备方法，包括如下的步骤：(1)将丁苯橡胶和顺丁橡胶置于密炼机内进行密炼，依次加入白炭黑、单宁酸、氧化锌和硬脂酸，混炼均匀后排料，冷却备用；(2)将第一步制得的胶料投入开炼机，完全包辊后加入促进剂、硫黄，吃料完全后割刀，薄通，下片，停放备用。

【技术特征摘要】
1.一种单宁酸改性白炭黑补强丁苯橡胶的制备方法，包括如下的步骤：(1)将丁苯橡胶和顺丁橡胶置于密炼机内进行密炼，依次加入白炭黑、单宁酸、氧化锌和硬脂酸，混炼均匀后排料，冷却备用；(2)将第一步制得的胶料投入开炼机，完全包辊后加入促进剂、硫黄，吃料完全后割刀，薄通，下片，停放备用。2.根据权利要求1所述的单宁酸改性白炭黑补强丁苯橡胶的制备方法，其特征在于：所述步骤(1)中，丁苯橡胶和顺丁橡胶的密炼时间为2-5分钟。3...

【专利技术属性】
技术研发人员：沈梅，马晨，侯占峰，辛振祥，
申请(专利权)人：青岛科技大学，
类型：发明
国别省市：山东,37