单元线圈相互串套抗拉人造革制造技术
Unit coils interlaced with tensile artificial leather
The invention relates to a unit coil interlacing and pulling artificial leather, which is composed of a substrate layer (1), an adhesive layer (2), a reinforcing layer (3), an adhesive layer (2) and a surface layer (4) from bottom to top. A backing fabric layer is formed on the back surface of the matrix layer, and the lining fabric layer is a knitted fabric, which is made of continuous coil units, and the continuous unit coil is made of stainless steel fiber. The invention has good elasticity and tension. The unit coils of the invention are interconnected with each other.
【技术实现步骤摘要】
单元线圈相互串套抗拉人造革
本专利技术涉及一种人造革。
技术介绍
市场上出售的人造革一般是由基质层、粘合层和面层组成，具有比较差的抗拉性能，容易断裂，性能上难以满足人们日益提高的质量要求。
技术实现思路
本专利技术的目的在于克服上述不足，提供一种不易断裂的抗拉人造革。本专利技术的目的是这样实现的：一种单元线圈相互串套抗拉人造革，从下往上依次由基质层、粘合层、加强层、粘合层和面层组成，所述加强层为纺织物和纤维组成，所述基质层由以下重量份数的原料组成：聚氯乙烯树脂36~45份；增塑剂18～26份；增韧剂8~14份；稳定剂0.8~1.7份；填料9~15份；大豆油2~4份；润滑剂0.3~0.9份；黑色糊0.5~1.1份。所述基质层背面复合有衬里织物层，所述衬里织物层，为一种针织物，由连续的单元线圈相互串套而成，连续的单元线圈由不锈钢纤维制成。与现有技术相比，本专利技术的有益效果是：本专利技术由于基质层和面层中还设有纺织物和纤维组成的加强层，可以增加人造革的抗拉性能，获得良好的弹性和张力，不易断裂，满足多领域使用。本专利技术所提供的针织物，通过使用不锈钢纤维，使用其所制备的针织物具有致密的金属网络，可以有效屏蔽电磁波，屏蔽效能在50dB-80dB。并且具有强度高、柔软性好，耐600℃～1000℃高温，耐各种酸碱的化学腐蚀强的优势，使其能够应用于强腐蚀、高温烟气等高温环境及军工领域。附图说明图1为本专利技术的结构示意图。其中：基质层1、粘合层2、面层3、加强层4。具体实施方式参见图1，本专利技术涉及的一种单元线圈相互串套抗拉人造革，从下往上依次由基质层1、粘合层2、加强层...
【技术保护点】
一种单元线圈相互串套抗拉人造革，其特征在于所述人造革从下往上依次由基质层（1）、粘合层（2）、加强层（3）、粘合层（2）和面层（4）组成，所述加强层（4）为纺织物和纤维组成，所述基质层由以下重量份数的原料组成：聚氯乙烯树脂 36~45 份；增塑剂 18 ～ 26 份；增韧剂 8~14 份；稳定剂 0.8~1.7 份；填料 9~15 份；大豆油 2~4 份；润滑剂 0.3~0.9 份；黑色糊 0.5~1.1 份；所述基质层背面复合有衬里织物层，所述衬里织物层，为一种针织物，由连续的单元线圈相互串套而成，连续的单元线圈由不锈钢纤维制成。
【技术特征摘要】
1.一种单元线圈相互串套抗拉人造革，其特征在于所述人造革从下往上依次由基质层（1）、粘合层（2）、加强层（3）、粘合层（2）和面层（4）组成，所述加强层（4）为纺织物和纤维组成，所述基质层由以下重量份数的原料组成：聚氯乙烯树脂36~45份；增塑剂18～...
【专利技术属性】
技术研发人员：王东，
申请(专利权)人：江阴永隆塑料有限公司，
类型：发明
国别省市：江苏,32