Luminous paint and method of the invention discloses a preparation method of the building, by weight of the number of components: 45 polyvinyl butyral 60, strontium aluminate 1 powder 1 3 copies, 2 copies, 8 copies of the 5 curing agent, film-forming agent 7 12, leveling agent 8 12 copies, 90 copies of 30 water, thickening agent 3 5 copies, 8 copies of 5 luminous pigment. The present invention by the above formula for preparation of luminescent paint good luminous performance, and long continuance, in building wall surface is easy to form a smooth surface, can be long-term continuous luminous coating, solves the problem of short duration and poor performance of existing luminescent paint coatings, also reduces the cost and simplify the preparation method of coating.
【技术实现步骤摘要】
一种建筑用发光涂料及其制备方法
本专利技术涉及涂料领域，尤其涉及一种建筑用发光涂料及其制备方法。
技术介绍
目前，建筑用外墙一般都采用涂料涂装，涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧的保护膜，建筑涂料具有装饰功能、保护功能和居住性改进功能。各种功能所占的比重因使用目的不同而不尽相同。装饰功能是通过建筑物的美化来提高它的外观价值的功能。随着人们审美观念的进步，对建筑发光涂料的需求越来越大，如在城市中涂上发光涂料可以作为广告牌使用，传统需要灯具装饰，电控发光，浪费能源，海边的灯塔在夜间也需要照明，如果停电，则失去了灯塔原有的功能，目前的发光涂料采用在建筑用涂料中加荧光粉的办法，持续时间短，起不到实际使用的效果。因此，现有技术还有待于改进和发展。
技术实现思路
鉴于上述现有技术的不足，本专利技术的目的在于提供一种建筑用发光涂料及其制备方法，旨在解决现有发光涂料发光时间短的问题。本专利技术的技术方案如下：一种建筑用发光涂料，按重量份数计由以下组分组成：聚乙烯醇缩丁醛45-60份；铝酸锶1-3份；磁粉1-2份；固化剂5-8份；成膜剂7-12份；流平剂8-12份；...
【技术保护点】
一种建筑用发光涂料，其特征在于，按重量份数计由以下组分组成：聚乙烯醇缩丁醛45‑60份；铝酸锶1‑3份；磁粉1‑2份；固化剂5‑8份；成膜剂7‑12份；流平剂8‑12份；水30‑90份；增稠剂3‑5份；发光颜料5‑8份。
【技术特征摘要】
1.一种建筑用发光涂料，其特征在于，按重量份数计由以下组分组成：聚乙烯醇缩丁醛45-60份；铝酸锶1-3份；磁粉1-2份；固化剂5-8份；成膜剂7-12份；流平剂8-12份；水30-90份；增稠剂3-5份；发光颜料5-8份。2.根据权利要求1所述的建筑用发光涂料，其特征在于，所述磁粉由铁鳞粉、铁红、硫酸钡按照质量比1：1：1的比例配制而成。3.根据权利要求1所述的建筑用发光涂料，其特征在于，所述成膜剂由三聚氰酸环氧，丙二醇苯醚，丁醚醋酸酯，磷酸二氢盐，沥青乳剂，刺槐豆胶，半乳甘露糖中的一种或几种组成。4.根据权利要求1所述的建筑用发光涂料，其特征在于，所述流平剂由陶土，焦磷酸四钠，环氧树脂，纳米SiO2-Ag抗菌剂，聚醚改性有机硅，丁酮，丁酯，氮氮二甲基甲酰胺中的一种或几种组成。5.根据权利要求1所述的建筑用发光涂料，其特征在于，所述增稠剂由...
【专利技术属性】
技术研发人员：陈强，
申请(专利权)人：佛山市三水区嫚娅环保科技有限公司，
类型：发明
国别省市：广东,44