The invention discloses a laser quenching technology of laser quenching with light absorbing coating and preparation method thereof, the laser quenching with a light absorbing coating comprises the following components: silica: 80 100; 150 industrial alcohol 200; 10 binder: 20; metal oxide 15 25 thickening; agent 12 18 and 3 8 rosin, the laser quenching with a light absorbing coating preparation method comprises the following steps: S1: silica: 80 100; 10 binder: 20; metal oxide 15 25; thickener 12 18 copies and 8 copies of 3 rosin into the ball milling machine for milling; S2: step S1 milled raw materials into 150 200 industrial alcohol, stirring evenly, greatly improves the hardness of the workpiece to avoid local burn the workpiece, the ball mill for milling on light absorbing coating, can greatly improve the suction The performance of light coating makes the particle size of the absorbable coating uniform and refined, and the invention is low cost and does not pollute the environment.
【技术实现步骤摘要】
一种激光淬火用吸光涂料及其制备方法
本专利技术涉及激光淬火
，具体为一种激光淬火用吸光涂料及其制备方法。
技术介绍
激光淬火是激光表面处理技术中应用最早的一项技术,是一种快速、局部的淬火工艺。主要利用激光束扫描工件表面后,将材料表面温度快速加热到相变温度以上熔点以下,并依靠工件基体本身的导热将热量迅速向基体内部传递,达到快速冷却淬火的目的。这一过程是通过固态自冷却淬火即固态相变重结晶,改变表面组织结构而产生强化效果,淬火后可获得一定厚度的硬化层。激光淬火对提高机械零件的机械性能有其独特的效果,特别是它解决了常规热处理引起的变形和精度下降等问题,在应用中受到关注。激光表面淬火处理时，为避免金属表面对激光辐射光能的吸收率过低，淬火前，需在被处理的金属表面上涂覆一层吸光涂料以提高金属表面的光热转换率。现有的吸光涂料价格昂贵，不便于工业化生产，且会造成环境的污染，热稳定性差，为此，我们提出一种激光淬火用吸光涂料及其制备方法。
技术实现思路
本专利技术的目的在于提供一种激光淬火用吸光涂料及其制备方法，以解决上述
技术介绍
中提出的现有的吸光涂料价格昂贵，不便于工业化生产，且会...
【技术保护点】
一种激光淬火用吸光涂料，其特征在于：该激光淬火用吸光涂料包括如下组成成分：二氧化硅：80‑100份；工业酒精150‑200份；粘结剂：10‑20份；金属氧化物15‑25份；增稠剂12‑18份和松香3‑8份。
【技术特征摘要】
1.一种激光淬火用吸光涂料，其特征在于：该激光淬火用吸光涂料包括如下组成成分：二氧化硅：80-100份；工业酒精150-200份；粘结剂：10-20份；金属氧化物15-25份；增稠剂12-18份和松香3-8份。2.根据权利要求1所述的一种激光淬火用吸光涂料，其特征在于：所述工业酒精的百分比浓度为96-98%。3.根据权利要求1所述的一种激光淬火用吸光涂料，其特征在于：所述的金属氧化物采用锰系氧化物。4.根据权利要求1所述的一种激光淬火用吸光涂料，其特征在于：所述粘结剂为虫胶。5.一种激光淬火用吸光涂料的制备方法，其特征在于：该激光淬火用...
【专利技术属性】
技术研发人员：许正茂，金开瑞，
申请(专利权)人：徐州万达回转支承有限公司，
类型：发明
国别省市：江苏,32