The invention relates to a multifunctional UV coating, the coating weight includes the following components: anti yellowing agent 23 antibacterial agent 1 28 copies, 3 copies, 20 copies of the antistatic agent 5 monomer, 16 27 copies, 2 photo initiator 5, leveling agent 2 8 copies, 36 copies of 28 inert solvent. The present invention by adding conductive nano attapulgite in UV coating, activated by silane coupling agent, adding anti yellowing agent, antibacterial agent and other raw materials, overcome the defects of traditional waterborne antistatic properties, antibacterial effect, anti yellowing performance difference. The anti yellow additive of the present invention adopts the combination of acrylic resin and alkyd resin to achieve very good yellow effect.
【技术实现步骤摘要】
一种多功能UV涂料
本专利技术涉及一种UV涂料，特别涉及一种多功能UV涂料。
技术介绍
UV就是紫外线(Ultra-VioletRay)的英文简称。工业用的UV波长以200nm到400nm为其应用范围。用UV来照射“UV照射可硬化的材料”而使它硬化。UV涂料可通过浸涂、淋涂、漆涂、旋涂，甚至真空涂等方法涂布后，再经紫外线光子照射而固化成膜。顾名思义，UV涂料的固化是和UV光的照射分不开的。UV固化涂料起源于70年代的国际涂料市场，是一种全新的绿色技术。利用该技术生产的紫外光固化涂料，简称UV涂料。20世纪末，UV固化涂料开始流行于西方、日本等地，是一种代表时尚的涂料品种。UV固化涂料最早应用于手机、DVD、随身听外壳的表面涂装处理，后来其应用领域现进一步扩展到化妆品、电视机及电脑等家用电器领域。UV光固化涂料具有不含挥发性有机化合物(VOC)，对环境污染小，固化速度快，节省能源、固化产物性能好、适合于高速自动化生产等优点。而传统涂料易挥发、固化速度慢，不利于环境保护。因此，UV涂料是传统涂料的主要替代品。UV涂料因应用领域不同而成分各异，但其基本组成可归纳为：1....
【技术保护点】
一种多功能UV涂料，其特征在于，所述UV涂料包括如下重量份数的组分：抗变黄助剂23‑28份、抗菌助剂1‑3份、抗静电助剂5‑20份、单体16‑27份、光引发剂2‑5份、流平剂2‑8份、惰性溶剂28‑36份。
【技术特征摘要】
1.一种多功能UV涂料，其特征在于，所述UV涂料包括如下重量份数的组分：抗变黄助剂23-28份、抗菌助剂1-3份、抗静电助剂5-20份、单体16-27份、光引发剂2-5份、流平剂2-8份、惰性溶剂28-36份。2.根据权利要求1所述的多功能UV涂料，其特征在于，所述抗变黄助剂由丙烯酸树脂和醇酸树脂组成，所述丙烯酸树脂与醇酸树脂的重量比为1:1-2。3.根据权利要求2所述的多功能UV涂料，其特征在于，所述丙烯酸树脂选自二异氰酸酯、二异氰酸甲苯酯、二异氰酸亚己基酯、双酚A环氧丙烯酸酯中的一种或多种。4.根据权利要求2所述的多功能UV涂料，其特征在于，所述醇酸树脂选自干性醇酸树脂。5.根据权利要求1所述的多功能UV涂料，其特征在于，所述抗菌助剂为纳米二氧化钛。6.根据权利要...
【专利技术属性】
技术研发人员：方杰敏，
申请(专利权)人：桂林市漓江机电制造有限公司，
类型：发明
国别省市：广西,45