The invention belongs to the technical field of fire retardant coating, is a kind of fire retardant coatings for steel structure, which is composed of the following parts by weight of raw materials: 325 300-400 cement, gypsum powder 100-150, 40-80 bentonite and calcium carbonate powder 100-150, high temperature aluminum silicate fiber 30-50, water 400-500; during the preparation of high temperature aluminum silicate fiber made of glue solution in the water, and then the 325 cement, gypsum powder, bentonite, heavy calcium carbonate powder mixed evenly and glue mixing, stirring, the coating of the invention; all the inorganic, non-toxic, odorless, harmless material, safety and environmental protection, excellent fire resistance, after heating no harmful gases, production low cost, simple preparation process, suitable for wide application.
【技术实现步骤摘要】
本专利技术属于防火涂料
，具体是一种钢结构防火涂料。
技术介绍
随着城市化进程的高速发展，大量高楼平地而起，随之而来的问题是如何保证高层建筑物的防火安全问题，目前的建筑物均是框架结构板房，在建筑中使用了大量钢材，如何作好钢结构表面防火工作成为重中之重。一般的防火材料均添加有有机阻燃剂，在起火时虽然可以起到阻燃效果，但是有机阻燃剂在遇到高温时容易挥发出有毒气体，对人体同样会造成危险，因此，研发一种建筑专用的安全环保的无机防火涂料十分必要。
技术实现思路
本专利技术的目的就是针对目前建筑物中使用的防火涂料很多都含有有机阻燃剂，在遇到高温时容易挥发出有毒物质，对人体造成危害的问题，而提供一种钢结构防火涂料。本专利技术的一种钢结构防火涂料,由下述重量份原料组成：325水泥300-400石膏粉100-150膨润土40-80重质碳酸钙粉100-150高温硅酸铝纤维30-50水400-500；制备时，高温硅酸铝纤维溶于水中制成胶液，然后将325水泥、石膏粉、膨润土、重质碳酸钙粉混合均匀后与胶液混合，搅拌均匀，即得。本专利技术涂料在使用之，直接刷在建筑物钢结构（梁、柱等）外表面，涂层厚度需达到19mm以上。本专利技术涂料耐火极限最少可达2小时，涂层厚度越厚，阻燃时间越长。本专利技术涂料全部采用无机、无毒、无味、无害物质制成，安全环保，耐火性能优异，加热后无有害气体产生，生产成本低廉，制备工艺简单，适合广泛推广应用。具体实施方式实施例1本实施例...
【技术保护点】
一种钢结构防火涂料,其特征在于由下述重量份原料组成：325水泥 300‑400 石膏粉 100‑150膨润土 40‑80 重质碳酸钙粉 100‑150高温硅酸铝纤维 30‑50 水 400‑500；制备时，高温硅酸铝纤维溶于水中制成胶液，然后将325水泥、石膏粉、膨润土、重质碳酸钙粉混合均匀后与胶液混合，搅拌均匀，即得。
【技术特征摘要】
1.一种钢结构防火涂料,其特征在于由下述重量份原料组成：
325水泥300-400石膏粉100-150
膨润土40-80重质碳酸钙粉100-150
高温硅酸铝纤...