一种利用冷冻干燥制备复合材料的方法技术
A method of preparation of composite materials by freeze drying
The invention discloses a method of using freeze drying composite material preparation method is as follows: the lignin or hydroxyethyl cellulose to prepare aqueous solution by freeze-drying to obtain lignin aerogel or hydroxyethyl cellulose aerogels, aerogel mixed matrix resin and the carbon aerogel or after the uniform, with mixed double screw extrusion, the prepared composite materials are described, the matrix resin is polypropylene or polyethylene. The invention adopts freeze-drying method simple lignin or hydroxyethyl cellulose after drying, flake loose structure of the auxiliary material, and the matrix resin was prepared by mixing of polymer composite materials, this method effectively improves the mixing effect between lignin or hydroxyethyl cellulose and the matrix resin, improve the solubility of added material in the matrix resin, thus improving the performance of composite material preparation.
【技术实现步骤摘要】
一种利用冷冻干燥制备复合材料的方法
本专利技术属于复合材料制备领域，具体涉及一种利用冷冻干燥制备复合材料的方法。
技术介绍
木质素是一种储量丰富、可再生的重要资源，在制备可降解、可再生的高分子复合材料方面有着重要的发展前景。但是，许多非极性高分子如聚丙烯、聚乙烯，由于与木质素之间的相容性很差，在制备复合材料过程中，木质素难以和基体材料混合均匀，因而不能较好的发挥复合效果，对材料性能的改进有限。现有提高添加助剂在基体材料中分散性的方法有通过研磨等方式改变粒径，或改变添加助剂的极性等，但是这些方法效果有限，效率不高，而且改性方法复杂。采用制备纳米材料的方法也可改善添加助剂与基体材料的相容性，但是纳米材料制备方法复杂，成本相对较高。如公开号为CN102604307A的专利技术专利公开了一种新型聚丙烯复合材料，该专利技术通过用含双键酯化剂与木质素中羟基发生酯化反应，并进一步将改性木质素与取代烯烃单体接枝，从而降低木质素中羟基基团，增加改性后木质素与聚丙烯的相容性，该方法虽然可以提高木质素在聚丙烯基体中的分散性，但是改性方法步骤繁杂。
技术实现思路
针对现有技术存在的上述不足，...
【技术保护点】
一种利用冷冻干燥制备复合材料的方法，其特征在于，将木质素或羟乙基纤维素配制成水溶液，经冷冻干燥后得到木质素气凝胶或羟乙基纤维素气凝胶，将得到的气凝胶与基体树脂混合均匀，用双螺杆混合挤出，即制备得到所述的复合材料，所述基体树脂为聚丙烯或聚乙烯。
【技术特征摘要】
1.一种利用冷冻干燥制备复合材料的方法，其特征在于，将木质素或羟乙基纤维素配制成水溶液，经冷冻干燥后得到木质素气凝胶或羟乙基纤维素气凝胶，将得到的气凝胶与基体树脂混合均匀，用双螺杆混合挤出，即制备得到所述的复合材料，所述基体树脂为聚丙烯或聚乙烯。2.根据权利要求1所述的利用冷冻干燥制备复合材料的方法，其特征在于，所述气凝胶与基体树脂混合前，先将气凝胶置于管式炉中于氩气气氛中碳化。3.根据权利要求1或2所述的利用冷冻干...