For a Aluminum Alloy household air conditioner composite pipe, consists of the following raw materials: Si:0.04 mass percentage of 0.08%; Fe:0.33 0.40%; Cu:0.05 0.1%; Mn:1.0 1.1%; the rest is Al; the optimal composition: Si:0.06%; Fe:0.35%; Cu:0.08%; Mn:1.05%; the rest is Al; impurity content: Mg = 0.02; Zn = 0.02; Ti = 0.05; Cr = 0.01; Pb = 0.01. The aluminum alloy composite pipe manufactured by the invention can be used as an important part of the condenser of the household air conditioner. Compared with the traditional copper alloy pipe, the composite pipe has the advantages of small density, good bend pipe, light weight, environmental protection, synergy, energy saving, and low cost.
【技术实现步骤摘要】
用于家用空调复合管材的铝合金及其制备方法
本专利技术涉及铝合金材料
，尤其是涉及一种用于家用空调复合管材的铝合金及其制备方法。
技术介绍
空调热交换管道的材料大多为铁合金或铜合金，但是目前铁管性能不佳，而铜管价格较高。随着空调产业的不断发展，家用空调开始从铜管进入到铝管的时代。空调体积越小越好，所以必须选择热交换效率好于或者与铜接近的材料才能替代；其次空调的工作环境恶劣，对制冷管路系统的防腐要求高。目前常规的采用铝管制作的家用空调散热器在防腐蚀方面略逊于铜管。为降低成本和提高性能，研制新的适用于家用空调复合管材的铝合金是必要的。
技术实现思路
针对现有技术存在的上述问题，本申请提供了一种用于家用空调复合管材的铝合金及其制备方法。本专利技术制备得到的铝合金复合管材可以作为家用空调冷凝器重要组成部分，同传统的铜合金管材相比，复合管材具有密度小、弯管好、重量轻、环保、增效、节能、降本等优点。本专利技术的技术方案如下：一种用于家用空调复合管材的铝合金，由以下质量百分数的原料组成：Si：0.04-0.08％；Fe：0.33-0.40％；Cu：0.05-0.1％；Mn：1....
【技术保护点】
一种用于家用空调复合管材的铝合金，其特征在于由以下质量百分数的原料组成：Si：0.04‑0.08％；Fe：0.33‑0.40％；Cu：0.05‑0.1％；Mn：1.0‑1.1％；余量为Al；杂质含量：Mg≤0.02；Zn≤0.02；Ti≤0.05；Cr≤0.01；Pb≤0.01。
【技术特征摘要】
1.一种用于家用空调复合管材的铝合金，其特征在于由以下质量百分数的原料组成：Si：0.04-0.08％；Fe：0.33-0.40％；Cu：0.05-0.1％；Mn：1.0-1.1％；余量为Al；杂质含量：Mg≤0.02；Zn≤0.02；Ti≤0.05；Cr≤0.01；Pb≤0.01。2.根据权利要求1所述的铝合金，其特征在于由以下质量百分数的原料组成：Si：0.06％；Fe：0.35％；Cu：0.08％；Mn：1.05％；余量为Al；杂质含量：Mg≤0.02；Zn≤0.02；Ti≤0.05；Cr≤0.01；Pb≤0.01。3.权利要求1或2所述的铝合金的制备方法，其特征在于具体步骤如下：(1)投炉前，用耙子对炉底、炉侧壁进行清理干净；(2)把纯度为99.7％的铝锭投入炉子中，开火对铝锭进行熔化；熔化温度控制在720-740℃；熔化时间4-5小时(3)然后打开氩气，压力调整在0.08-0.12Mpa；对铝液进行精炼20-30分钟，把表面的浮渣清理干净，对铝液进行取样分析；(4)根据分析数值加入铁剂和锰剂，搅拌10-15分钟，进行第二次精炼，精炼...