The purpose of the present invention is to provide a sealant for a liquid crystal display element that can take into account the low temperature curing and the preservation of the stability. In addition, the aim of the present invention is to provide an upper and lower conduction material and a liquid crystal display element for using the sealant to use the liquid crystal display element. The invention relates to a liquid crystal display element is the sealant, heat curing resin and curing agent containing liquid crystal display with sealant element, the curable resin containing curable resin with epoxy group, the heat curing agent containing epoxy resin and has the structure from structure to self amine compound amine adduct compounds as the amine compounds, amine compounds is the source for the number of alkyl alkyl imidazole 1~20.
【技术实现步骤摘要】
【国外来华专利技术】液晶显示元件用密封剂、上下导通材料及液晶显示元件
本专利技术涉及能够兼顾低温固化性和保存稳定性的液晶显示元件用密封剂。另外，本专利技术还涉及使用该液晶显示元件用密封剂而成的上下导通材料及液晶显示元件。
技术介绍
近年来，就液晶显示单元等液晶显示元件的制造方法而言，从生产节拍时间的缩短、使用液晶量的最优化的观点出发，采用的是专利文献1、专利文献2所公开那样的使用含有固化性树脂、光聚合引发剂和热固化剂的光热并用固化型的密封剂的被称作滴下工艺的方式。在滴下工艺中，首先，在2个带电极的基板中的一个基板上利用分配形成长方形的密封图案。接着，在密封剂未固化的状态下将液晶的微小滴滴加到基板的密封框内，并在真空下重叠另一基板，对密封部照射紫外线等光，进行预固化。之后，加热而进行主固化，制作液晶显示元件。现在该滴下工艺成为液晶显示元件的制造方法的主流。从节能化、液晶的稳定性的观点出发，期望利用低温且短时间的加热使上述密封剂热固化。作为用于利用低温且短时间的加热使密封剂固化的方法，以往使用的是熔点低的热固化剂、固化促进剂。然而，若使用熔点低的热固化剂或固化促进剂，则即使在室温附近也容...
【技术保护点】
一种液晶显示元件用密封剂，其特征在于，其是含有固化性树脂和热固化剂的液晶显示元件用密封剂，所述固化性树脂含有具有环氧基的固化性树脂，所述热固化剂含有具有来自环氧树脂的结构和来自胺化合物的结构的胺加合化合物，成为所述胺加合化合物的来源的胺化合物是烷基的碳数为1～20的烷基咪唑。
【技术特征摘要】
【国外来华专利技术】2015.10.26 JP 2015-2100511.一种液晶显示元件用密封剂，其特征在于，其是含有固化性树脂和热固化剂的液晶显示元件用密封剂，所述固化性树脂含有具有环氧基的固化性树脂，所述热固化剂含有具有来自环氧树脂的结构和来自胺化合物的结构的胺加合化合物，成为所述胺加合化合物的来源的胺化合物是烷基的碳数为1～20的烷基咪唑。2.根据权利要求1所述的液晶显示元件用密封剂，其特征在于，烷基的碳数为1～20的烷基咪唑是2－甲基咪唑。3.根据权利要求1或2所述的液晶显示元件用密封剂，其特征在于，成为胺加合化合物的来源的环氧树脂具有芳香环。4.根据权利要求1、2或3所述的液晶显示元件用密封剂，其特征在于，成为...
【专利技术属性】
技术研发人员：小林洋，
申请(专利权)人：积水化学工业株式会社，
类型：发明
国别省市：日本,JP