Processing technology of non cleaning film covered profile
The invention provides a free cleaning film profile processing technology, through the reverse rotation brush polishing method, the PVC profile extrusion molding after the surface tension increases, in the film does not need cleaning, avoid the environmental pollution caused by volatile cleaning agent, can be used directly for hot melt adhesive film, and the film adhesion is stronger. The process includes the following steps: 1) will be placed in the PVC section above the brush, and contact with the PVC profile, PVC profile moving forward; 2) motor drive toward the opposite direction brush PVC profile moving direction of rotation, eliminating the release agent material surface composition by friction between the brush and the PVC profile.
【技术实现步骤摘要】
一种免清洗覆膜型材加工工艺
本专利技术属于型材加工领域，具体涉及一种免清洗覆膜型材加工工艺。
技术介绍
近年来，随着PVC型材的使用范围越来越广，客户对型材表面的颜色和花纹要求越来越多，覆膜型材的需求越来越大，在覆膜过程中，传统的覆膜工艺是在覆膜前先通过清洗剂进行清洗，洗掉PVC型材表面的PE蜡等析出物，然后再进行膜的贴合。清洗剂一般为酮类或苯类，均易挥发，容易造成空气污染。
技术实现思路
为了解决以上问题，本专利技术提供了一种免清洗覆膜型材加工工艺，通过毛刷逆向旋转抛光法，使PVC型材挤出成型后表面张力增大，在覆膜时不需要进行清洗，避免了清洗剂挥发造成的环境污染，可以直接使用热溶胶进行覆膜，而且膜的粘合牢度更强。该加工工艺具体包括如下步骤：1）将毛刷置于PVC型材上方，并与PVC型材接触,PVC型材向前移动；2）电机驱动毛刷朝向PVC型材移动方向的反方向旋转，通过毛刷与PVC型材之间的摩擦消除型材表面的脱模剂成分。作为优选，所述电机的功率为550W，转速为2900转/分。与现有技术相比，本专利技术借鉴ASA表面共挤型材表面顺向旋转抛光的原理，采用毛刷逆向旋转抛光的方法，提高PVC型材的表面张力。在PVC型材加工过程中，通过电机带动毛刷对PVC型材进行抛光，毛刷的旋转方向与PVC型材的牵引方向相反，从而能够更好的清除PVC型材表面的脱模剂成分。使PVC型材表面张力增大，在覆膜时不需要进行清洗，直接使用热熔胶进行覆膜，避免了因清洗剂造成的污染，同时型材和膜的粘合牢度更强。附图说明图1为本专利技术提供的消除型材表面脱模剂成分的清洗装置的结构简易图。具体实施方式实施...
【技术保护点】
一种免清洗覆膜型加工工艺，其特征在于：该工艺包括如下步骤： 1）将毛刷（1）置于PVC型材（2）上方，并与PVC型材（2）接触, PVC型材（2）向前移动；2）电机驱动毛刷（1）朝向PVC型材（2）移动方向的反方向旋转，通过毛刷（1）与PVC型材（2）之间的摩擦消除型材表面的脱模剂成分。
【技术特征摘要】
1.一种免清洗覆膜型加工工艺，其特征在于：该工艺包括如下步骤：1）将毛刷（1）置于PVC型材（2）上方，并与PVC型材（2）接触,PVC型材（2）向前移动；2）电机驱动毛刷（1）朝向PVC型材（2...