The invention discloses a vamp rubber insulated shoes, characterized in that, according to the weight calculation, including: natural rubber, 0.7 0.9, 100 sulfur accelerator M 0.4 0.6, accelerator D 0.3 0.5, accelerator DM 0.2 0.4, 0.9, 0.7 accelerator TMTD Zinc Oxide 1.9 2.1, stearic acid 1.4, antioxidant A 1.6 0.4 0.6, 0.8 antioxidant D 1.2, calcium carbonate, talc 20, 67 montan wax 0.8 1.2, 1.4 1.6, paraffin zinc stearate 1.9 2.1, oil 1.2 1.4. The use of natural rubber, improve the dielectric properties; reduce the amount of sulfur and accelerator TMTD instead of part of the sulphur content; the small absorption of calcium carbonate and talc powder combined with good insulation properties; the vamp with rubber insulating boots the formula production, low cost, can adapt to electrical operating environment protection applicable to electrical operation.
【技术实现步骤摘要】
一种绝缘鞋用鞋面胶
本专利技术涉及橡胶材料制备领域，涉及鞋用鞋面胶配方，尤其涉及一种绝缘鞋用鞋面胶。
技术介绍
普通橡胶材料制成的鞋子，其鞋面胶通常为天然橡胶加上合成橡胶，使用范围广、成本低，但由于部分合成橡胶介电性能较低，造成鞋面胶绝缘性较差，胶料中常用的促进剂、防老剂大多含有硫或氮，即使使用量极少，也会影响电性能，含有极性大的促进剂、防老剂的胶料，吸水性大，介电性能更会明显下降，常用的填充剂和补强剂炭黑会导致橡胶的电性能下降，因此，常用的鞋面胶配方并不能用于电工作业的防护。
技术实现思路
本专利技术的目的是针对现有技术的不足，而提供一种绝缘鞋用鞋面胶，用该配方生产的绝缘鞋用鞋面胶其绝缘性能较好，成本较低，能适应电工的操作环境，用于电工作业的防护。实现本专利技术目的的技术方案是：一种绝缘鞋用鞋面胶，按照重量份计算，包括：天然橡胶100、硫磺0.7-0.9、促进剂M0.4-0.6、促进剂D0.3-0.5、促进剂DM0.2-0.4、促进剂TMTD0.7-0.9、氧化锌1.9-2.1、硬脂酸1.4-1.6、防老剂A0.4-0.6、防老剂D0.8-1.2、碳酸钙67、滑石粉...
【技术保护点】
一种绝缘鞋用鞋面胶，其特征在于，按照重量份计算，包括：天然橡胶100、硫磺0.7‑0.9、促进剂M 0.4‑0.6、促进剂D 0.3‑0.5、促进剂DM 0.2‑0.4、促进剂TMTD 0.7‑0.9、氧化锌1.9‑2.1、硬脂酸1.4‑1.6、防老剂A 0.4‑0.6、防老剂D 0.8‑1.2、碳酸钙 67、滑石粉20、蒙旦蜡 0.8‑1.2、石蜡 1.4‑1.6、硬脂酸锌1.9‑2.1、油溶黑1.2‑1.4。
【技术特征摘要】
1.一种绝缘鞋用鞋面胶，其特征在于，按照重量份计算，包括：天然橡胶100、硫磺0.7-0.9、促进剂M0.4-0.6、促进剂D0.3-0.5、促进剂DM0.2-0.4、促进剂TMTD0.7-0.9、氧化锌1.9-2.1、硬脂酸1.4-1.6、防老剂A0.4-0.6、防老剂D0.8-1.2、碳酸钙67、滑石粉20、蒙旦蜡0.8-1.2、石蜡1.4-1.6、硬...