The invention discloses a rubber surface with upper insulation rubber boots, characterized in that, according to the weight calculation, including: natural rubber, 0.7 0.9, 100 sulfur accelerator M 0.4 0.6, accelerator D 0.3 0.5, accelerator DM 0.2 0.4, accelerator TMTD 0.7 0.9 Zinc Oxide 1.9, 2.1, 1.4 stearic acid 1.6, antioxidant A 0.6, antioxidant 0.4 D 0.8 1.2, talcum powder 87, 1.2, 0.8 montan wax paraffin 1.4 1.6, zinc stearate 1.9 2.1, oil 1.2 1.4. The natural rubber is used to improve dielectric properties, reduce sulfur consumption and use talc powder with small water absorbency. The insulation shoe made of this formula has better insulation performance and lower cost, and it can adapt to the operation environment of electrician, and is suitable for the protection of electrician operation.
【技术实现步骤摘要】
一种胶面绝缘靴用鞋面胶
本专利技术涉及橡胶材料制备领域，涉及鞋用鞋面胶配方，尤其涉及一种胶面绝缘靴用鞋面胶。
技术介绍
普通橡胶材料制成的鞋子，其鞋面胶通常为天然橡胶加上合成橡胶，使用范围广、成本低，但由于部分合成橡胶介电性能较低，造成鞋面胶绝缘性较差，胶料中常用的促进剂、防老剂大多含有硫或氮，即使使用量极少，也会影响电性能，含有极性大的促进剂、防老剂的胶料，吸水性大，介电性能更会明显下降，常用的填充剂和补强剂炭黑会导致橡胶的电性能下降，因此，常用的鞋面胶配方并不能用于电工作业的防护。
技术实现思路
本专利技术的目的是针对现有技术的不足，而提供一种胶面绝缘靴用鞋面胶，用该配方生产的胶面绝缘靴用鞋面胶其绝缘性能较好，成本较低，能适应电工的操作环境，用于电工作业的防护。实现本专利技术目的的技术方案是：一种胶面绝缘靴用鞋面胶，按照重量份计算，包括：天然橡胶100、硫磺0.7-0.9、促进剂M0.4-0.6、促进剂D0.3-0.5、促进剂DM0.2-0.4、促进剂TMTD0.7-0.9、氧化锌1.9-2.1、硬脂酸1.4-1.6、防老剂A0.4-0.6、防老剂D0.8-1.2...
【技术保护点】
一种胶面绝缘靴用鞋面胶，其特征在于，按照重量份计算，包括：天然橡胶100、硫磺0.7‑0.9、促进剂M 0.4‑0.6、促进剂D 0.3‑0.5、促进剂DM 0.2‑0.4、促进剂TMTD 0.7‑0.9、氧化锌1.9‑2.1、硬脂酸1.4‑1.6、防老剂A 0.4‑0.6、防老剂D 0.8‑1.2、滑石粉87、蒙旦蜡 0.8‑1.2、石蜡 1.4‑1.6、硬脂酸锌1.9‑2.1、油溶黑1.2‑1.4。
【技术特征摘要】
1.一种胶面绝缘靴用鞋面胶，其特征在于，按照重量份计算，包括：天然橡胶100、硫磺0.7-0.9、促进剂M0.4-0.6、促进剂D0.3-0.5、促进剂DM0.2-0.4、促进剂TMTD0.7-0.9、氧化锌1.9-2.1、硬脂酸1.4-1.6、防老剂A0.4-0.6、防老剂D0.8-1.2、滑石粉87、蒙旦蜡0.8-1.2、石蜡1.4-1.6、硬...