The invention discloses a bridge grouting material and a method for rapidly repairing the bridge expansion joint, which belongs to the technical field of bridge engineering. The grouting material including cement, sand, stones and water, the weight percentage of each component are as follows: cement: Sand: Gravel: water weight ratio of 5:3 to 8:10:6 ~ 7; among them, the cement weight contains the following components: sulphoaluminate cement 45 55 ordinary portland cement 8; 15; 2 expansion agent 7; 0.2 crack fiber filler 8 0.8; 20; 0.03 0.5 early strength agent. The invention realizes fast hardening, fast hardening and early strength, so that the compressive strength of the grouting material is more than 30MPa after 3 hours, and the traffic can be opened in 3 hours.
【技术实现步骤摘要】
桥梁灌浆料及采用其快速修复桥梁伸缩缝的方法
本专利技术属于桥梁工程
，涉及一种桥梁灌浆料，以及采用该桥梁灌浆料快速修复桥梁伸缩缝的方法。
技术介绍
目前，由于车辆超载、交通量的增大，道路施工工期较紧，施工质量欠佳，使得桥梁伸缩缝处的混凝土表面发生不同程度的破坏，容易引起车辆通过时产生跳跃的现象，给行车通过的人们带来了极大的安全隐患。现有桥梁伸缩缝的灌浆料大部分使用普通混凝土，但是，普通混凝土的强度发展缓慢，延长了桥梁的使用(通车)时间，且新旧普通混凝土的粘结强度低，抗裂性能差，大大缩短了桥梁的使用寿命。因此，亟需提出一种能够解决现有普通混凝土由于强度发展缓慢而延长使用时间，以及新旧混凝土粘结强度低、抗裂性能差而导致桥梁使用寿命短等问题的桥梁灌浆料，以及采用上述桥梁灌浆料快速修复桥梁伸缩缝的方法。
技术实现思路
(一)要解决的技术问题为了解决现有技术的上述问题，本专利技术提供一种具有快凝快硬、抗裂性能好、粘结力强、中后期强度更高的桥梁灌浆料。本专利技术还提供一种采用上述桥梁灌浆料快速修复桥梁伸缩缝的方法，该方法能够使桥梁在3个小时后即可开放，实现快速通车。(二)技...
【技术保护点】
一种桥梁灌浆料，其特征在于，所述灌浆料包括水泥、黄砂、石子和水，各组分的重量百分比如下：水泥:黄砂:石子:水的重量比为5:3～8:10:6～7；其中，所述水泥包含如下重量份数的组分：硫铝酸盐水泥 45‑55份普通硅酸盐水泥 8‑15份膨胀剂 2‑7份抗裂纤维 0.2‑0.8份填充料 8‑20份早强剂 0.03‑0.5份。
【技术特征摘要】
1.一种桥梁灌浆料，其特征在于，所述灌浆料包括水泥、黄砂、石子和水，各组分的重量百分比如下：水泥:黄砂:石子:水的重量比为5:3～8:10:6～7；其中，所述水泥包含如下重量份数的组分：硫铝酸盐水泥45-55份普通硅酸盐水泥8-15份膨胀剂2-7份抗裂纤维0.2-0.8份填充料8-20份早强剂0.03-0.5份。2.如权利要求1所述的桥梁灌浆料，其特征在于，所述水泥包含如下重量份数的组分：硫铝酸盐水泥48-50份普通硅酸盐水泥10-12份膨胀剂4-6份抗裂纤维0.4-0.6份填充料12-16份早强剂0.2-0.35份。3.如权利要求1所述的桥梁灌浆料，其特征在于，所述硫铝酸盐水泥为42.5级快硬低碱度硫铝酸盐水泥。4.如权利要求1所述的桥梁灌浆料，其特征在于，所述膨胀剂为铝酸钙类膨胀剂、氧化镁型膨胀剂和石灰系膨胀剂中的一种或一种以上的混合物。5.如权利要求1所述的桥梁灌浆料，其特征在于，所述早强剂为三乙醇胺、氯化钙、硝酸钾、硝酸钙中的一种或一种以上的混合物。6.如权利要求1所...
【专利技术属性】
技术研发人员：叶学林，
申请(专利权)人：合肥卡勒斯通建筑材料有限公司，
类型：发明
国别省市：安徽,34