The invention relates to the field of decorative materials, in particular to a plant fiber slurry suitable for GRC injection and a preparation method. The plant fiber pulp is made up of raw materials including the following weight parts: 100 sulphoaluminate cement, 5~15 vegetable fiber, 25~55 water, 0~15 admixture and 0.5 to 4 fiber glass fiber. The preparation method comprises the following steps: adding the admixture to the water at 15~25 degree temperature, stirring 1min, adding the sulphoaluminate cement, stirring 2min, adding the plant fiber and glass fiber and stirring 3min. The plant fiber slurry density smaller and smaller mass per unit area, easy handling and transfer, and can be nailed, saw better; is suitable for GRC injection, formed in the process of spraying layer compacted, without artificial pressure, greatly reduce the labor cost.
【技术实现步骤摘要】
一种适用于GRC喷射的植物纤维料浆及其制备方法
本专利技术涉及装饰材料领域，尤其涉及一种适用于GRC喷射的植物纤维料浆及其制备方法。
技术介绍
GRC或称GFRC中文为玻璃纤维增强水泥(混凝土)制品。如今GRC装饰产品被广泛的应用于建筑外墙装饰、室内装饰、园林景观及仿真工艺等诸多方面。现在市场上GRC产品的材料主要为水泥、砂、玻璃纤维、水、颜料及各种外加剂。现有的GRC产品大多存在如下缺陷：(1)采用砂石作为骨料密度大，大型产品质量大，不利于安装。(2)以砂石作为骨料在喷射过程中形成的料层比较松散，需人工辅助压平。(3)砂石作为骨料产品硬度高但是脆性也比较大，容易破损及开裂，不可钉、不可锯。
技术实现思路
(一)要解决的技术问题本专利技术要解决的技术问题是提供了一种密度小、韧性好且适用于GRC喷射的植物纤维料浆。(二)技术方案为了解决上述技术问题，本专利技术提供了一种适用于GRC喷射的植物纤维料浆，其由包括如下重量份的原料制备而成：硫铝酸盐水泥100份，植物纤维5～15份，水25～55份，外加剂0～15份，以及玻璃纤维0.5～4份。所述重量份为μg，mg，g，kg等本...
【技术保护点】
一种适用于GRC喷射的植物纤维料浆，其特征在于，由包括如下重量份的原料制备而成：硫铝酸盐水泥100份，植物纤维5～15份，水25～55份，外加剂0～15份，以及玻璃纤维0.5～4份。
【技术特征摘要】
1.一种适用于GRC喷射的植物纤维料浆，其特征在于，由包括如下重量份的原料制备而成：硫铝酸盐水泥100份，植物纤维5～15份，水25～55份，外加剂0～15份，以及玻璃纤维0.5～4份。2.根据权利要求1所述的适用于GRC喷射的植物纤维料浆，其特征在于，包括如下重量份的成分：硫铝酸盐水泥100份，植物纤维8～12份，水30～50份，外加剂5～10份，以及玻璃纤维1.5～3份。3.根据权利要求1或2所述的适用于GRC喷射的植物纤维料浆，其特征在于，所述植物纤维为锯末。4.根据权利要求3所述的适用于GRC喷射的植物纤维料浆，其特征在于，所述锯末的粒度为2～80目。5.根据权利要求4所述的适用于GRC喷射的植物纤维料浆，其特征在于，所述锯末的粒度为3...
【专利技术属性】
技术研发人员：杨卓舒，康璐，何伟志，
申请(专利权)人：河北卓达建材研究院有限公司，
类型：发明
国别省市：河北,13