一种玻璃纤维注射引拔工艺制造技术

一种玻璃纤维注射引拔工艺，包括如下步骤：1）玻璃纤维首先在导纱器和预成型模中初步成型，然后进入连续树脂传递模塑模具中；2）在连续树脂传递模塑模具的模具注胶仓中以稳定的高压和流量注入专用树脂，使得玻璃纤维充分在连续树脂传递模塑模具中充分浸透和排除气泡。3）充分浸透和不含气泡较少的玻璃纤维经由牵引机的牵引进入固化成型模具内。本发明专利技术工艺受环境的影响小，尤其是受湿度的影响小。充分保证产品的稳定性和一致性。

An injection drawing process for glass fiber injection

A glass fiber injection drawing process, which comprises the following steps: 1) in the first glass fiber yarn and pre forming die in initial shape, and then enter the continuous resin transfer molding mold; 2) mold plastic injection mold in continuous resin transfer molding chamber in a stable pressure and flow into the special resin, making glass fiber in the fully continuous resin transfer and remove air bubbles is fully saturated with molding mold. 3) the glass fiber that is fully soaked and does not contain little bubbles into the curing mold through the traction of the tractor. The invention of the invention is less influenced by the environment, especially the influence of humidity. Fully guarantee the stability and consistency of the product.

【技术实现步骤摘要】
一种玻璃纤维注射引拔工艺
本专利技术涉及玻璃纤维生产工艺，特别是一种玻璃纤维注射引拔工艺。
技术介绍
传统的玻璃纤维生产的玻璃纤维,微气泡的含量高,产品的性能差,容易出现夹杂和结纱等缺陷。且生产制造工艺容易受到环境特别是湿度的影响，生产出的玻璃纤维的稳定性和一致性能差，给后续的使用厂家带来很大的问题和损失。
技术实现思路
针对上述情况，为克服现有技术之缺陷，本专利技术之目的就是提供一种一种玻璃纤维注射引拔工艺，使得生产出的玻璃纤维的稳定性能好，且生产过程受生产环境影响小。其解决方案是，一种玻璃纤维注射引拔工艺，其特征在于，包括如下步骤：1）玻璃纤维首先在导纱器和预成型模中初步成型，然后进入连续树脂传递模塑模具中；2）在连续树脂传递模塑模具的模具注胶仓中以稳定的高压和流量注入专用树脂，使得玻璃纤维充分在连续树脂传递模塑模具中充分浸透和排除气泡。3）充分浸透和不含气泡较少的玻璃纤维经由牵引机的牵引进入固化成型模具内。4）经过牵引机的玻璃纤维经由切割装置切割成段。优选地，专用树脂为环氧树脂和甲基四氢邻苯二甲酸酐。本专利技术工艺受环境的影响小，尤其是受湿度的影响小。玻璃纤维充分浸透，所生产的FR本文档来自技高网...

【技术保护点】
一种玻璃纤维注射引拔工艺，其特征在于，包括如下步骤：1）玻璃纤维首先在导纱器和预成型模（1）中初步成型，然后进入连续树脂传递模塑模具（2）中；2）在连续树脂传递模塑模具（2）的模具注胶仓中以稳定的高压和流量 入专用树脂，使得玻璃纤维充分在连续树脂传递模塑模具（2）中充分浸透和排除气泡；3）充分浸透和不含气泡较少的玻璃纤维经由牵引机（3）的牵引进入固化成型模具（7）内；4）经过牵引机（3）的玻璃纤维经由切割装置（4）切割成段。

【技术特征摘要】
1.一种玻璃纤维注射引拔工艺，其特征在于，包括如下步骤：1）玻璃纤维首先在导纱器和预成型模（1）中初步成型，然后进入连续树脂传递模塑模具（2）中；2）在连续树脂传递模塑模具（2）的模具注胶仓中以稳定的高压和流量入专...